Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.10	%
Melt Mass-Flow Rate	380°C/2.16 kg	ASTM D1238	7.0	g/10 min
Modeling Shrinkage	Flow : 3.18 mm	ASTM D955	0.10 到 0.30	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.18 mm	ASTM D955	1.2 到 1.4	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Compressive Strength		ASTM D695	182	Mpa
Shearing Strength		ASTM D732	89.0	Mpa
Tensile Stress	Yield, 5.00 mm	ISO 527-2/1A/5	188	Mpa
Tensile Stress	Tensile Stress	-- 6	ASTM D638	191	Mpa
Tensile Modulus	-- 5	ASTM D638	15100	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1A/1	16700	Mpa
Tensile Elongation	Break 5	ASTM D638	1.8	%
Tensile Elongation	Tensile Elongation	Break	ISO 527-2/1A/5	1.8	%
Flexural Modulus	--	ASTM D790	14800	Mpa
Flexural Modulus	Flexural Modulus	--	ISO 178	15400	Mpa
Flexural Strength	23°C	ASTM D790	253	Mpa
	Flexural Strength	250°C	ASTM D790	54.0	Mpa
	Flexural Strength	Flexural Strength	--	ISO 178	250	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Peak Melting Temperature		ASTM D3418	345	°C
Glass Transition Temperature		ASTM D3418	150	°C
Specific Heat	50°C	DSC	1260	J/kg/°C
Specific Heat	Specific Heat	200°C	DSC	1620	J/kg/°C
Thermal Conductivity		ASTM E1530	0.31	W/m/K
Coefficient of Linear Thermal Expansion (Flow)	-50 to 50°C	ASTM E831	1.5E-5	cm/cm/°C
Deflection Temperature Under Load?	1.8 MPa, Annealed	ASTM D648	285	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	60 Hz	ASTM D150	2.0E-3
	Dissipation Factor?	1 kHz	ASTM D150	1.0E-3
	Dissipation Factor?	Dissipation Factor?	1 MHz	ASTM D150	3.0E-3
Dielectric Strength		ASTM D149	19	KV/mm
Surface Resistivity		ASTM D257	> 1.9E+17	ohms
Dielectric Constant	60 Hz	ASTM D150	3.68
	Dielectric Constant	1 kHz	ASTM D150	3.69
	Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.66
Volume Resistivity		ASTM D257	1.8E+17	ohms·cm

Fill Analysis	Test Condition	Test Method	Test Result	Unit
Melt Viscosity	400°C, 1000 sec^-1	ASTM D3835	450	Pa·s

Injection	Test Result	Unit
Drying Time	2.5 到 4.0	hr
Back Pressure	0.138 到 0.345	Mpa
Screw Speed	75	rpm
Spiral Flow	2.0:1.0
Drying Temperature	150 到 175	°C
Processing (Melt) Temp	370 到 395	°C
Mold Temperature	175 到 210	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	--	ASTM D4812	590	J/m
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	--	ISO 180	41	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	105

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.8 mm	UL 94	V-1
Flame Rating	Flame Rating	1.6 mm	UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.