Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 380℃，5.0kg | ISO 1133 | 7 | g/10min |
| Moisture Absorption | 23℃，24hr，3.20 mm | ISO 62-1 | 0.05 | % |
| Moisture Absorption | Equilibrium，23℃，3.20 mm | ISO 62-1 | 0.4 | % |
| Modeling Shrinkage | MD | ISO 294-4 | 0.7 | % |
| Modeling Shrinkage | TD | ISO 294-4 | 0.2 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | Break，23℃ | ISO 527 | 205 | Mpa |
| Flexural Strength | Break，23℃ | ISO 178 | 310 | Mpa |
| Flexural Modulus | 23℃ | ISO 178 | 16000 | Mpa |
| Tensile Strain | Break，23℃ | ISO 527 | 2 | % |
| Shore Hardness | 23℃ | ISO 868 | 86 | D 级 |
| Electrical | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | 23 ℃，1V | IEC 60093 | 10^7 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 7 | kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1U | 45 | kJ/m² |
| Notched Izod Impact Strength | 有Notched | ISO 180-A | 8 | kJ/m² |
| Notched Izod Impact Strength | | ISO 180/U | 40 | kJ/m² |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.8 Mpa | ISO 75-f | 325 | °C |
| Coefficient of Linear Thermal Expansion | 低于Tg沿着Flow | ISO 11359 | 8 | ppm/K |
| Coefficient of Linear Thermal Expansion | 高于Tg沿着Flow | ISO 11359 | 8 | ppm/K |
| Melting Temperature | | ISO 11357 | 343 | °C |
| Glass Transition Temperature | 起始 | ISO 11357 | 143 | °C |
| Specific Heat | 23℃ | DSC | 1.8 | kJ/kg/℃ |
| Thermal Conductivity | 23℃ | ISO 22007-4 | 0.95 | W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.