Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 380℃，5.0kg | ISO 1133 | 6.5 | g/10min |
| Moisture Absorption | 23℃，24hr，3.2 mm厚拉伸棒 | ISO 62-1 | 0.05 | % |
| Moisture Absorption | Equilibrium，23℃ | ISO 62-1 | 0.4 | % |
| Modeling Shrinkage | MD | ISO 294-4 | 0.8 | % |
| Modeling Shrinkage | TD | ISO 294-4 | 0.3 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | Break，23℃ | ISO 527 | 155 | Mpa |
| Flexural Strength | Break，23℃ | ISO 178 | 245 | Mpa |
| Flexural Modulus | 23℃ | ISO 178 | 8800 | Mpa |
| Tensile Strain | Break，23℃ | ISO 527 | 3.3 | % |
| Shore Hardness | 23℃ | ISO 868 | 85 | D 级 |
| Compressive Strength | 23℃ | ISO 604 | - | Mpa |
| Electrical | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | 2 mm | IEC 60243-1 | 24 | KV/mm |
| Dissipation Factor | 23℃，1 MHz | IEC 60250 | 0.005 | |
| Comparative Tracking Index | | IEC 60112 | 150 | V |
| Dielectric Constant | 23 ℃, 1 kHz | IEC 60250 | 3.1 | |
| Volume Resistivity | 23 ℃，1V | IEC 60093 | 10^16 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | | ISO 179/1U | 45 | kJ/m² |
| Charpy Notched Impact Strength | | ISO 179-1eA | 7 | kJ/m² |
| Notched Izod Impact Strength | | ISO 180/A | 7.5 | kJ/m² |
| Unnotched Izod Impact Strength | | ISO 180/U | 60 | kJ/m² |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal Conductivity | 23℃ | ISO 22007-4 | 0.3 | W/m/K |
| Heat Deflection Temperature | 1.8 Mpa | ISO 75-f | 315 | °C |
| Coefficient of Linear Thermal Expansion | 低于Tg沿着Flow | ISO 11359 | 20 | ppm/K |
| Coefficient of Linear Thermal Expansion | 高于Tg沿着Flow | ISO 11359 | 22 | ppm/K |
| Melting Temperature | | ISO 11357 | 343 | °C |
| Glass Transition Temperature | | ISO 11357 | 143 | °C |
| Specific Heat | 23℃ | DSC | 1.7 | kJ/kg /℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.