EVA Elvax® 150W DUPONT USA
107
- Unit Price:
- $2941 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 93MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:antioxidant Thermal stability
- Application Areas:blend sealant adhesive
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D1505 | 0.975 | g/cm² | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 45 | g/10min | |
| VA content | 33 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 190/2.16kg | ASTM D-1238/ISO 1133 | 43 | g/10min |
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 43 | g/10min |
| 190°C/2.16kg | ISO1133 | 43 | g/10min | |
| Vinyl acetate content | 32.0 | wt% | ||
| VA content | 32 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| melting point | DSC | ASTM D-3418/ISO 3146 | 63(145) | ℃(°F) |
| 63 | ℃（℉） | |||
| vicat softening point | ASTM D1525/ISO R306 | 36 | ℃（℉） | |
| ASTM D-1525/ISO 306 | 36(97) | ℃(°F) | ||
| Vicat softening temperature | ASTMD1525 | 36.0 | °C | |
| ISO306 | 36.0 | °C | ||
| Melting temperature (DSC) | ISO3146 | 63.0 | °C | |
| Peak melting temperature | ASTMD3418 | 63.0 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.