Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 0.70 | g/10min |
Vinyl Acetate Content | | | 14.0 | wt% |
Density / Specific Gravity | | ASTMD1505 | 0.934 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break | ASTMD638 | 750 | % |
Flexural Modulus | | ASTMD790 | 22.6 | Mpa |
Tensile Strength | Yield | ASTMD638 | 6.86 | Mpa |
Tensile Strength | Break | ASTMD638 | 19.6 | Mpa |
Coefficient of Friction | Blown Film | ASTMD1894 | 0.50 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTMD1525 | 75.0 | °C |
Brittleness Temperature | | ASTMD746 | -70.0 | °C |
Melting temperature | | | 90.0 | °C |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Film Thickness - Tested) | | | 50 | µm |
Secant Modulus | 1%Secant,MD:50μm,Blown Film | ASTMD882 | 36.3 | Mpa |
Secant Modulus | 1%Secant,TD:50μm,Blown Film | ASTMD882 | 41.2 | Mpa |
Tensile Elongation | MD:Break,50μm,Blown Film | ASTMD882 | 450 | % |
Tensile Elongation | TD:Break,50μm,Blown Film | ASTMD882 | 600 | % |
Elmendorf Tear Strength | MD:50μm,Blown Film | ASTMD1922 | 20 | g |
Elmendorf Tear Strength | TD:50μm,Blown Film | ASTMD1922 | 48 | g |
Tensile Strength | MD:Yield,50μm,Blown Film | ASTMD882 | 4.90 | Mpa |
Tensile Strength | TD:Yield,50μm,Blown Film | ASTMD882 | 3.92 | Mpa |
Tensile Strength | MD:Break,50μm,Blown Film | ASTMD882 | 30.4 | Mpa |
Tensile Strength | TD:Break,50μm,Blown Film | ASTMD882 | 27.5 | Mpa |
Gardner Impact | 50μm,Blown Film | ASTMD1709 | 620 | g |
Film Thickness | | | 1.2-5.9mil(30-150µ | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore A | ASTMD2240 | 9240 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Gloss | 45°,50.0μm,Blown Film | ASTMD2457 | 90 | |
Haze | 50.0μm,Blown Film | ASTMD1003 | 3.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.