PET Rynite® 935 NC010 DUPONT USA
88
- Unit Price:
- $2893 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 29.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High temperature resistan
- Application Areas:household electrical appl Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.58 |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 0.70 | % |
| MD | ISO294-4 | 0.30 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.83 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.13 | % | |
| MediumDensity | 1.32 | g/cm³ | ||
| Ejection Temperature | 170 | °C | ||
| SpecificHeatCapacityofMelt | 1790 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.32 | W/m/K | ||
| Modeling Shrinkage (Flow) | 3.20 mm | ASTM D955 | 0.0035 | cm/cm |
| Modeling Shrinkage (Across Flow) | 3.20 mm | ASTM D955 | 0.0065 | cm/cm |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 5.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Creep Modulus | 1hr | ISO899-1 | 9350 | Mpa |
| Unnotched Izod Impact Strength | ASTM D256 | 425 | J/m | |
| Tensile Strength | ASTM D695 | 141 | Mpa | |
| Tensile Elongation?(Break) | ASTM D638 | 2.0 | % | |
| Notched Izod Impact Strength | ASTM D256 | 43 | J/m | |
| Tensile Stress | Break | ISO527-2 | 85.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 2.0 | % |
| Notched Impact Strength | ASTM D256 | 64 | J/m | |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 7690 | Mpa |
| Tensile Modulus | ISO527-2 | 10200 | Mpa | |
| ASTM D412/ISO 527 | 10200 | kg/cm²(MPa)[Lb/in²] | ||
| ASTM D638 | 9930 | Mpa | ||
| Tensile Strength | ASTM D638 | 89.6 | Mpa | |
| Rockwell Hardness | ASTM D785 | 75 | ||
| Flexural Modulus | ASTM D790/ISO 178 | 9100 | kg/cm²(MPa)[Lb/in²] | |
| ASTM D790 | 9600 | Mpa | ||
| ISO178 | 9100 | Mpa | ||
| Flexural Strength | ASTM D790/ISO 178 | 141 | kg/cm²(MPa)[Lb/in²] | |
| ASTM D790 | 141 | Mpa | ||
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 2.0 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | UL 94 | HB | ||
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.6E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.6E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 5.2E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 5.3E-05 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 1.4E-07 | m²/s | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 235 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 200 | °C | |
| 66 psi， Unannealed | ASTM D648 | 241 | °C | |
| 264 psi，Unannealed | ASTM D648 | 215 | °C | |
| ASTM D648/ISO 75 | 235 | ℃（℉） | ||
| Melting Temperature | 252 | °C | ||
| Coefficient of Linear Thermal Expansion (Flow) | ASTM E831 | 0.000016 | cm/cm/ ℃ | |
| Vicat Softening Temperature | ISO306/B50 | 205 | °C | |
| Melting Temperature | ISO11357-3 | 252 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation Factor? | 100Hz | IEC60250 | 0.030 | |
| 1MHz | IEC60250 | 0.014 | ||
| Relative Permittivity | 100Hz | IEC60250 | 4.50 | |
| 1MHz | IEC60250 | 4.10 | ||
| Comparative Tracking Index | IEC60112 | 300 | V | |
| Dielectric Strength | IEC60243-1 | 39 | KV/mm | |
| Surface Resistivity | IEC60093 | 1E+14 | ohms | |
| Volume Resistivity | IEC60093 | 1E+15 | ohms·cm |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 280-300 | % |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 20 | kJ/m² |
| 23°C | ISO179/1eU | 25 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Sale | ISO2039-2 | 75 | |
| R-Sale | ISO2039-2 | 115 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS Flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.