PET Rynite® 530 NC010 DUPONT USA
175
- Unit Price:
- $3086 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 250.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced wear resistant High rigidity High temperature resistan Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electrical field Electronic field Household appliances Household appliances Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.75 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
| MD | ISO294-4 | 0.20 | % | |
| Melt Volume flow Rate | 280°C/2.16kg | ISO1133 | 6.00 | cm3/10min |
| Ejection Temperature | 170 | °C | ||
| Density / Specific Gravity | ISO1183 | 1.68 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Creep Modulus | 1hr | ISO899-1 | 11200 | Mpa |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 9700 | Mpa |
| Tensile Stress | Break | ISO527-2 | 135 | Mpa |
| Tensile Strain | Break | ISO527-2 | 2.0 | % |
| Tensile Modulus | ISO527-2 | 11500 | Mpa | |
| Flexural Modulus | ISO178 | 10500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 243 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 225 | °C | |
| RTIElec | 0.40mm | UL746 | 155 | °C |
| 0.75mm | UL746 | 155 | °C | |
| 1.5mm | UL746 | 155 | °C | |
| 3.0mm | UL746 | 155 | °C | |
| Evolution Calendar intelligent importer | 0.40mm | UL746 | 155 | °C |
| 0.75mm | UL746 | 155 | °C | |
| 1.5mm | UL746 | 155 | °C | |
| 3.0mm | UL746 | 155 | °C | |
| RTIStr | 0.40mm | UL746 | 155 | °C |
| 0.75mm | UL746 | 155 | °C | |
| 1.5mm | UL746 | 155 | °C | |
| 3.0mm | UL746 | 155 | °C | |
| EffectiveThermalDiffusivity | UL746 | 1.1E-07 | m²/s | |
| Vicat Softening Temperature | ISO306/B50 | 220 | °C | |
| Melting Temperature | ISO11357-3 | 252 | °C | |
| Linear thermal expansion coefficient | MD：-- | ISO11359-2 | 1.9E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.2E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 9.2E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 6.8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 39 | KV/mm | |
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Dissipation Factor? | 100Hz | IEC60250 | 7E-03 | |
| 1MHz | IEC60250 | 0.013 | ||
| Surface Resistivity | IEC60093 | 1E+14 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Relative Permittivity | 100Hz | IEC60250 | 4.80 | |
| 1MHz | IEC60250 | 4.30 | ||
| Comparative Tracking Index | IEC60112 | 200 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.35mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-05VA | ||
| 0.35mm | IEC60695-11-10,-20 | V-0 | ||
| 1.5mm | IEC60695-11-10,-20 | V-05VA | ||
| Oxygen Index | ISO4589-2 | 33 | % | |
| FMVSS Flammability | FMVSS302 | DNI |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.