PET Rynite® 415HP-NC010 DUPONT JAPAN
87
- Unit Price:
- $2495 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 19MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Electrical tools Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
| TD3 | ISO294-4 | 1.2 | % | |
| MD | ISO294-4 | 0.30 | % | |
| MD3 | ISO294-4 | 0.50 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 2.5 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.25 | % | |
| Melt Volume flow Rate | 280°C/2.16kg | ISO1133 | 4.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2 | 4700 | Mpa | |
| Flexural Modulus | ISO178 | 3550 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 79.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 5.0 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 2E-05 | cm/cm/°C |
| MD:-40to23°C | ISO11359-2 | 9.8E-05 | cm/cm/°C | |
| MD:55to160°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| TD | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD:-40to-23°C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| TD:55to160°C | ISO11359-2 | 3.2E-05 | cm/cm/°C | |
| EffectiveThermalDiffusivity | ISO11359-2 | 9E-08 | m²/s | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 235 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 207 | °C | |
| Melting Temperature | ISO11357-3 | 250 | °C | |
| Vicat Softening Temperature | ISO306/B50 | 205 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+13 | ohms | |
| Volume Resistivity | IEC60093 | 1E+13 | ohms·cm | |
| Comparative Tracking Index | CTI | UL746 | PLC2 | |
| Comparative Tracking Index | IEC60112 | 350 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 25 | kJ/m² |
| 23°C | ISO179/1eU | 55 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Sale | ISO2039-2 | 58 | |
| R-Sale | ISO2039-2 | 111 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94,IEC60695-11-10,-20 | HB | |
| 1.5mm | UL94,IEC60695-11-10,-20 | HB | ||
| Oxygen Index | ISO4589-2 | 19 | % | |
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.