TPE THERMOLAST® K TC8MLB-S340 KRAIBURG TPE GERMANY
57
- Unit Price:
- $6183 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD | 内部方法 | 0.40to0.70 | % |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 5.0 | g/10min |
| 200°C/5.0kg | ISO1133 | 5.0 | g/10min | |
| Density | ASTMD792 | 1.19 | g/cm³ | |
| 23°C | ISO1183 | 1.19 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | 屈服,23°C | ISO527-2 | 39.0 | Mpa |
| Flexural Stress | 23°C | ISO178 | 64.0 | Mpa |
| Tensile Strength | 23°C | ASTMD638 | 39.2 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 2500 | Mpa |
| 23°C | ISO178 | 2500 | Mpa | |
| Flexural Strength | 23°C | ASTMD790 | 64.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,12.7mm | ASTMD648 | 81.0 | °C |
| 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 81.0 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 93.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 93.0 | °C | |
| Vicat Softening Temperature | ISO306/A | 87.0 | °C | |
| ASTMD15253 | 87.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C,6.35mm | ISO180 | 220 | J/m |
| 23°C,6.35mm | ASTMD256 | 220 | J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.