PA6T Ultramid® TKR4355G10 BASF GERMANY
121
- Unit Price:
- $7190 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 21MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Thermal stability
- Application Areas:Engineering accessories Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 3.5 到 4.5 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.40 到 0.80 | % | |
| Shrinkage rate | Across Flow | ISO 294-4 | 0.66 | % |
| 流量 | ISO 294-4 | 0.20 | % | |
| Apparent density | 0.70 | g/cm³ | ||
| Stickiness number | 96% H2SO4 | ISO 307 | 135 | cm³/g |
| Mold Shrinkage - Constrained 3 | 0.29 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | -- | Mpa |
| Tensile stress | Break | ISO 527-2 | 240 | Mpa |
| Tensile strain | Break | ISO 527-2 | 2.4 | % |
| Tensile modulus | ISO 527-2 | 17000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 245 | °C |
| specific heat | 1000 | J/kg/°C | ||
| thermal conductivity | DIN 52612 | 0.32 | W/m/K | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C | ISO 11359-2 | 1.8E-5 | cm/cm/°C |
| Across Flow : 23 to 55°C | ISO 11359-2 | 5.0E-5 到 6.0E-5 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 285 | °C | |
| Maximum operating temperature - short cycle operation | 260 | °C | ||
| 温度指数 - at 50% loss of tensile strength | -- 5 | IEC 60216 | 170 | °C |
| -- 6 | IEC 60216 | 145 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1 MHz | IEC 60250 | 0.020 | |
| Dielectric strength | IEC 60243-1 | 33 | KV/mm | |
| Relative permittivity | 1 MHz | IEC 60250 | 4.70 | |
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| Surface resistivity | IEC 60093 | -- | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+17 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Residence Time | < 5.0 | min | ||
| Screw Speed | < 18 | m/min | ||
| drying temperature | 110 | °C | ||
| Suggested maximum moisture content | 0.15 | % | ||
| Processing (melt) temperature | 310 到 330 | °C | ||
| Mold temperature | 80 到 120 | °C | ||
| drying time | 8.0 | hr | ||
| Temperature at the rear of the barrel | 300 | °C | ||
| Temperature in the middle of the barrel | 310 | °C | ||
| Temperature at the front of the material cylinder | 320 | °C | ||
| Spray nozzle temperature | 320 | °C | ||
| Hopper temperature | 80 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 85 | kJ/m² |
| 23°C | ISO 179/1eU | 90 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Polymer Abbreviation | PA6T/6-GF50 | |||
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.