Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | ISO 294-4 | 1.3 | % |
Modeling Shrinkage | 流量 | ISO 294-4 | 0.33 | % |
Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.28 | % |
Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 1.5 | % |
Spiral Flow?3,?4 | | | 9.00 | CM |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | | ISO 178 | 190 | Mpa |
Tensile Stress | Break | ISO 527-2 | 125 | Mpa |
Tensile Strain | Break | ISO 527-2 | 2.2 | % |
Tensile Modulus | | ISO 527-2 | 10000 | Mpa |
Flexural Modulus | | ISO 178 | 8400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 315 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 285 | °C |
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 1.8E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 6.0E-5 | cm/cm/°C |
Glass Transition Temperature | | ISO 11357-2 | 125 | °C |
Melting Temperature | | ISO 11357-3 | 325 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 5.00 GHz | IEC 60250 | 0.014 | |
Relative Permittivity | 5.00 GHz | IEC 60250 | 3.73 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 27 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flammability level | 0.75 mm | IEC 60695-11-10, -20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.