Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | 120°C | ISO 527-2 | 8200 | Mpa |
Tensile Modulus | 160°C | ISO 527-2 | 7400 | Mpa |
Flexural Modulus | 120°C | ISO 178 | 7300 | Mpa |
Flexural Modulus | 160°C | ISO 178 | 6500 | Mpa |
Tensile Stress | 160°C | ISO 527-2 | 120 | Mpa |
Tensile Stress | 120°C | ISO 527-2 | 140 | Mpa |
Charpy Notched Impact Strength | 23°C | ISO 180-1A | 16 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO 180-1A | 16 | kJ/m² |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | | ISO 11359-2 | 0.000025 | cm/cm/°C |
Melting temperature | | ISO 3146 | 295 | °C |
Deflection Temperature Under Load? | 1.8MPa | ISO 75-1 | 290 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC 60093 | 1E+14 | ohm*cm |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO294-4 | 0.9 | % |
Moisture Absorption | 23°C/50%RH | ISO 62 | 1.9 | % |
Density | | ISO 1183 | 1.62 | g/cm³ |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.