PA612 SC315 NC010 DUPONT USA
88
- Unit Price:
- $4973 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | Across Flow | ISO 294-4 | 1.4 | % |
流量 | ISO 294-4 | 1.3 | % | |
Moisture Absorption | Saturation, 23°C, 2.00 mm | ISO 62 | 3.0 | % |
Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.3 | % | |
Viscosity number | 96% H2SO4 | ISO 307 | 95.0 | cm³/g |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Stress | Yield | ISO 527-2 | 62.0 | Mpa |
Tensile Strain | Yield | ISO 527-2 | 4.5 | % |
Tensile Modulus | ISO 527-2 | 2400 | Mpa | |
Flexural Modulus | ISO 178 | 2100 | Mpa | |
Nominal Tensile Strain at Break | ISO 527-2 | 17 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Vicat Softening Temperature | ISO 306/B50 | 181 | °C | |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 135 | °C |
1.8 MPa, Unannealed | ISO 75-2/A | 62.0 | °C | |
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 1.1E-4 | cm/cm/°C |
Flow : -40 to 23°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
Flow : 55 to 160°C | ISO 11359-2 | 1.6E-4 | cm/cm/°C | |
Across Flow | ISO 11359-2 | 1.2E-4 | cm/cm/°C | |
Across Flow : -40 to 23°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
Across Flow : 55 to 160°C | ISO 11359-2 | 1.8E-4 | cm/cm/°C | |
Melting Temperature | ISO 11357-3 | 218 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Dielectric Strength | IEC 60243-1 | 30 | KV/mm | |
Relative Permittivity | 1 MHz | IEC 62631-2-1 | 3.20 | |
100 Hz | IEC 62631-2-1 | 3.60 | ||
Comparative Tracking Index | IEC 60112 | 600 | V | |
Volume Resistivity | IEC 62631-3-1 | 1.0E+13 | ohms·m | |
Dissipation Factor? | 100 Hz | IEC 62631-2-1 | 0.014 | |
1 MHz | IEC 62631-2-1 | 0.016 |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melt Density | 0.900 | g/cm³ | ||
Specific Heat Capacity of Melt | 2750 | J/kg/°C | ||
Thermal Conductivity of Melt | 0.18 | W/m/K | ||
Emission of Organic Compounds | VDA 277 | 3.10 | µgC/g |
Extrusion | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying Temperature | 80 | °C | ||
Drying Time | 3.0 到 4.0 | hr | ||
Suggested Max Moisture | 0.060 | % | ||
Melt Temperature | 235 到 250 | °C | ||
Extrusion Melt Temperature, Optimum | 240 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Drying time - Hot air dryer | 2.0 到 4.0 | hr | ||
Suggested Max Moisture | 0.15 | % | ||
Processing (Melt) Temp | 230 到 290 | °C | ||
Melt Temperature, Optimum | 250 | °C | ||
Mold Temperature | 50 到 90 | °C | ||
Mold Temperature, Optimum | 70 | °C | ||
Holding Pressure | 50.0 到 100 | Mpa | ||
Drying Recommended | yes | |||
Hold Pressure Time | 4.00 | s/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
23°C | ISO 179/1eU | 无断裂 |
hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Rockwell Hardness | R -Sale | ISO 2039-2 | 114 |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Oxygen Index | ISO 4589-2 | 27 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.