PA612 Zytel® 77G43L NC010 DUPONT USA
147
- Unit Price:
- $4850 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability high strength
- Application Areas:Electronic and Electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 0.80 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| Moisture Absorption | Saturation, 23°C, 2.00 mm | ISO 62 | 1.7 | % |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 0.70 | % | |
| Viscosity number | ISO 307 | 145 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO 527-2 | 200 | Mpa |
| Tensile Strain | Break | ISO 527-2 | 3.0 | % |
| Tensile Modulus | ISO 527-2 | 12500 | Mpa | |
| Flexural Modulus | ISO 178 | 11000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 217 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 203 | °C | |
| Linear thermal expansion coefficient | Flow | ISO 11359-2 | 1.4E-5 | cm/cm/°C |
| Flow : -40 to 23°C | ISO 11359-2 | 2.1E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 1.3E-5 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 65.0 | °C | |
| Melting Temperature | ISO 11357-3 | 218 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | IEC 62631-3-1 | 1.0E+13 | ohms·m |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ejection Temperature | 210 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 80 | °C | ||
| Drying time - Hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested Max Moisture | 0.20 | % | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Melt Temperature, Optimum | 290 | °C | ||
| Mold Temperature | 70 到 120 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| Holding Pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 85 | kJ/m² |
| 23°C | ISO 179/1eU | 100 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R -Sale | ISO 2039-2 | 118 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning Rate | 1.00 mm | ISO 3795 | 21 | mm/min |
| Flame Rating | 0.71 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS Flammability | FMVSS 302 | B | ||
| Haze | ISO 6452 | 1.0E-4 | g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.