PA612 Zytel® 151L DUPONT USA
221
- Unit Price:
- $6468 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Photostability lubrication
- Application Areas:Non specific food Cosmetic
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 1.1 | % | |
| TD：3.20mm | 1.1 | % | ||
| TD | ISO294-4 | 1.4 | % | |
| MD | ISO294-4 | 1.3 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 3.0 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.3 | % | |
| MediumDensity | 0.900 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2750 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.18 | W/m/K | ||
| Stickiness number | 96%H2SO4 | ISO307 | 95.0 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2 | 62.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 4.5 | % |
| Tensile modulus | ISO527-2 | 2400 | Mpa | |
| Bending modulus | ISO178 | 2100 | Mpa | |
| Nominal tensile fracture strain | ISO527-2 | 17 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature 2 | ISO11357-2 | 65.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 135 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 62.0 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.6E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.8E-04 | cm/cm/°C | |
| Vicat softening temperature | ISO306/B50 | 181 | °C | |
| Melting temperature 2 | ISO11357-3 | 218 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 100Hz | IEC60250 | 0.014 | |
| 1MHz | IEC60250 | 0.016 | ||
| Relative permittivity | 100Hz | IEC60250 | 3.60 | |
| 1MHz | IEC60250 | 3.20 | ||
| Leakage Trace Index | IEC60112 | 600 | V | |
| Dielectric strength | IEC60243-1 | 30 | KV/mm | |
| Surface resistivity | IEC60093 | -- | ohms | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strain MD | Yield | ISO527-3 | 4.5 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 114 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.9mm | UL94 | V-2 | |
| 1.5mm | UL94 | V-2 | ||
| 0.9mm | IEC60695-11-10,-20 | V-2 | ||
| 1.5mm | IEC60695-11-10,-20 | V-2 | ||
| Extreme Oxygen Index | ISO4589-2 | 27 | % | |
| FMVSS flammability | FMVSS302 | DNI |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 3.10 | µgC/g | |
| Odor | VDA270 | 4.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.