Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | 2.00mm | 内部方法 | 0.40 | % |
| Melt Mass-Flow Rate | 200°C/5.0kg | ISO1133 | 3.1 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 47 | g/10min |
| Density / Specific Gravity | 23°C | ISO1183 | 1.09 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | | ISO527-2/5 | 36 | % |
| Tensile Stress | Yield | ISO527-2/5 | 51.0 | Mpa |
| Flexural Modulus | | ISO178 | 2400 | Mpa |
| Flexural Stress | | ISO178 | 72.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 65.0 | °C |
| Vicat Softening Temperature | | ISO306/B | 86.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | | ISO179 | 11 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Scale | ISO2039-2 | 39 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 2000µm | ISO14782 | 2.4 | % |
| Transmittance | 2000µm | ISO13468-1 | 91.0 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.