Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | % | 0.80 | -- |
| Modeling Shrinkage | MD | % | 0.80 | -- |
| Moisture Absorption | Saturation,23°C | % | 1.5 | -- |
| Moisture Absorption | Equilibrium,23°C,50%RH | % | 0.70 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield | MPa | 45.0 | 40.0 |
| Tensile Stress | Break | MPa | 60.0 | 50.0 |
| Tensile Strain | Yield | % | 10 | |
| Tensile Modulus | | MPa | 1400 | 1100 |
| Nominal Tensile Strain at Break | | % | >50 | ＞50 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Continuous Use Temperature | --2 | °C | 90.0到110 | -- |
| Continuous Use Temperature | --3 | °C | 150 | -- |
| Melting Temperature | | °C | 178 | -- |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | °C | 115 | -- |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | °C | 45.0 | -- |
| Linear thermal expansion coefficient | MD | cm/cm/°C | 1.2E-04 | -- |
| Linear thermal expansion coefficient | TD | cm/cm/°C | 1.4E-04 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | kV/mm | -- | |
| Comparative Tracking Index | | V | -- | 600 |
| Surface Resistivity | | ohms | -- | 1E+12 |
| Volume Resistivity | | ohms·cm | -- | 1E+13 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | | 无断裂 | 无断裂 |
| Charpy Unnotched Impact Strength | 23°C | | 无断裂 | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D,15sec | | -- | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 0.8mm | | HB | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.