PA12 LNP™ LUBRICOMP™ SCL36 SABIC INNOVATIVE US
36
- Unit Price:
- $9283 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 24.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 24hr | ASTM D955 | 0.040 到 0.060 | % |
| Across Flow : 24hr | ASTM D955 | 0.40 到 0.60 | % | |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.090 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.14 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.41 | |
| Static | ASTM D3702 | 0.30 | ||
| Specific Wear Rate | ASTM D3702 | 0.0 4.4E+6 | 10^-8 mm³/N·m | |
| Tensile Modulus | -- 1 | ASTM D638 | 21400 | Mpa |
| -- | ISO 527-2/1 | 19400 | Mpa | |
| Tensile Elongation | Break 2 | ASTM D638 | 1.9 | % |
| Break | ISO 527-2/5 | 1.0 | % | |
| Flexural Modulus | 50.0 mm Span 3 | ASTM D790 | 15800 | Mpa |
| -- 4 | ISO 178 | 16500 | Mpa | |
| Tensile Strength | Break 2 | ASTM D638 | 157 | Mpa |
| Break | ISO 527-2/5 | 130 | Mpa | |
| Flexural Stress | -- | ISO 178 | 206 | Mpa |
| Yield, 50.0 mm Span 3 | ASTM D790 | 215 | Mpa | |
| Break, 50.0 mm Span 3 | ASTM D790 | 214 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear thermal expansion coefficient | Flow : -30 to 30°C | ASTM D696 | 2.9E-5 | cm/cm/°C |
| Across Flow : -30 to 30°C | ASTM D696 | 6.3E-5 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 178 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Bf | 177 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 173 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Af | 170 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 4.0 | hr | ||
| Rear Temperature | 215 到 225 | °C | ||
| Middle Temperature | 220 到 230 | °C | ||
| Front Temperature | 225 到 240 | °C | ||
| Back Pressure | 0.200 到 0.300 | Mpa | ||
| Screw Speed | 30 到 60 | rpm | ||
| Drying Temperature | 80 | °C | ||
| Suggested Max Moisture | 0.12 到 0.20 | % | ||
| Processing (Melt) Temp | 225 到 240 | °C | ||
| Mold Temperature | 70 到 80 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 690 | J/m |
| 23°C 6 | ISO 180/1U | 39 | kJ/m² | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 14.0 | J |
| -- | ISO 6603-2 | 4.00 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.