PA12 Pebax® 7033 SP 01 ARKEMA USA

Unit Price:
$16944 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
32MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 294-4	1.5	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	1.2	%
Moisture Absorption	Saturation, 23°C	ISO 62	1.1	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Yield	ISO 527-2	23.0	Mpa
	Tensile Stress	Break	ISO 527-2	54.0	Mpa
		Tensile Stress	10% Strain	ISO 527-2	22.0	Mpa
		Tensile Stress	Tensile Stress	100% Strain	ISO 527-2	21.0	Mpa
Tensile Strain	Yield	ISO 527-2	22	%
Tensile Strain	Tensile Strain	Break	ISO 527-2	> 300	%
Tensile Modulus		ISO 527-2	414	Mpa
Nominal Tensile Strain at Break		ISO 527-2	> 50	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	99.0	°C
Vicat Softening Temperature		ISO 306/B50	164	°C
Coefficient of Linear Thermal Expansion (Flow)		ISO 11359-2	1.6E-4	cm/cm/°C
Melting Temperature		ISO 11357-3	172	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index		IEC 60112	--	V
Surface Resistivity		IEC 60093	--	ohms

Fill Analysis	Test Result	Unit
Melt Density	0.830	g/cm³
Specific Heat Capacity of Melt	2700	J/kg/°C
Thermal Conductivity	0.20	W/m/K

Extrusion	Test Result	Unit
Drying Temperature	70 到 80	°C
Drying Time	5.0 到 7.0	hr
Melt Temperature	220 到 250	°C

Injection	Test Result	Unit
Drying Temperature	70 到 80	°C
Processing (Melt) Temp	230 到 290	°C
Mold Temperature	25 到 60	°C
Drying Time	5.0 到 7.0	hr

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Shore Hardness	Shore D, 15 sec	ISO 7619-1	61

Flammability	Test Condition	Test Method	Test Result	Unit
Flammability level	1.6 mm	IEC 60695-11-10, -20	HB
Flammability level	Flammability level	3.1 mm	IEC 60695-11-10, -20	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.