Technical Data Sheet
| Electrical | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC 60093 | -- | ohms·cm |
| Comparative Tracking Index | | IEC 60112 | -- | V |
| Surface Resistivity | | IEC 60093 | -- | ohms |
| Dielectric Strength | | IEC 60243-1 | -- | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30℃ -30°C | ISO 179/1eU | -- | kJ/m² |
| Charpy Unnotched Impact Strength | 23℃ 23°C | ISO 179/1eU | -- | kJ/m² |
| Charpy Notched Impact Strength | -30℃ -30°C | ISO 179/1eA | -- | kJ/m² |
| Charpy Notched Impact Strength | 23℃ 23°C | ISO 179/1eA | -- | kJ/m² |
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ISO 1183 | 1.22 | g/cm³ |
| Moisture Absorption | Saturation，23℃ Saturation, 73°F | ISO 62 | 1.4 | % |
| Moisture Absorption | Equilibrium，23℃，50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 0.6 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | Break Break | ISO 527-2 | 120 | Mpa |
| Tensile Strain | Break Break | ISO 527-2 | 6 | % |
| Shore Hardness | Shore D，15 sec Shore D，15 sec | ISO 868 | -- | |
| Shore Hardness | 球压硬度 Ball Indentation Hardness | ISO 2039-1 | -- | Mpa |
| Shore Hardness | 拉伸模量 Tensile Modulus | ISO 527-2 | 6500 | Mpa |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.8 MPa，Unannealed 264 psi, Unannealed | ISO 75-2/A | 165 | °C |
| Heat Deflection Temperature | 8.0 MPa，Unannealed 1160 psi, Unannealed | ISO 75-2/C | 90 | °C |
| Melting Temperature | | ISO 11357-3 | 180 | °C |
| Continuous Use Temperature | -- -- 2 2 | ISO 2578 | 90.0 到 120 | °C |
| Continuous Use Temperature | -- -- 3 3 | 内部方法 | 150 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.