Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan Low temperature resistanc
Application Areas:Medical Supplies
Color:--
Grade:Flame retardant enhanced grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	1.4	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	1.2	%
Water absorption rate	Saturation, 23°C	ISO 62	1.2	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.60	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield	ISO 527-2	12.0	Mpa
	Tensile stress	Break	ISO 527-2	52.0	Mpa
		Tensile stress	10% Strain	ISO 527-2	10.0	Mpa
		Tensile stress	Tensile stress	100% Strain	ISO 527-2	14.0	Mpa
Tensile strain	Yield	ISO 527-2	25	%
Tensile strain	Tensile strain	Break	ISO 527-2	> 300	%
Tensile modulus		ISO 527-2	170	Mpa
Nominal tensile fracture strain		ISO 527-2	> 50	%
abrasion resistance		ISO 4649	47.0	mm³

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion - flow		ISO 11359-2	1.7E-4	cm/cm/°C
Melting temperature 2		ISO 11357-3	159	°C
Vicat softening temperature		ISO 306/B50	142	°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	66.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	--	ohms
Volume resistivity		IEC 60093	3.2E+13	ohms·cm
Dissipation factor	100 Hz	IEC 60250	0.11
Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.10
Dielectric strength		IEC 60243-1	39	KV/mm
Relative permittivity	100 Hz	IEC 60250	9.00
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	5.00
Leakage Trace Index		IEC 60112	--	V

elastomer	Test Condition	Test Method	Test Result	Unit
Permanent compression deformation	23°C	ISO 815	43	%

Filling analysis	Test Result	Unit
Thermal conductivity of melt	0.18	W/m/K
Melt density	0.830	g/cm³
Specific Heat Capacity of Melt	2800	J/kg/°C

injection	Test Result	Unit
drying temperature	65 到 75	°C
Processing (melt) temperature	200 到 270	°C
Mold temperature	25 到 60	°C
drying time	4.0 到 6.0	hr

squeeze	Test Result	Unit
drying temperature	65 到 75	°C
drying time	4.0 到 6.0	hr
Melt Temperature	210 到 230	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Supporting hardness	Shore D, 15 sec	ISO 7619-1	50

flammability	Test Condition	Test Method	Test Result	Unit
Flammability level	1.6 mm	IEC 60695-11-10, -20	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.