Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.02 | kg·cm/cm(J/M)ft·lb/in |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.25 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | ISO 294-4 | 0.9/0.9 | % |
Moisture Absorption | | ISO 62 | 0.6 | % |
Melting Temperature | | ISO 11357-3 | 179 | °C |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Strain (Field) | | ISO 527-1/-2 | 4 | % |
Tensile Strength(Yield) | | ISO 527-1/-2 | 47 | Mpa |
Shore Hardness | | ISO 868 | 77 | D |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 3C | KJ/m |
Charpy Notched Impact Strength | -40℃ | ISO 179/1eA | 3C | KJ/m |
Tensile Elongation | Break | ISO 527-1/-2 | >200 | % |
Rockwell Hardness | | ASTM D785 | 110 | |
Rockwell Hardness | | ISO 2039-2 | 105 | R |
Flexural Modulus | | ASTM D412/ISO 527 | 14500 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO 178 | 1500 | Mpa |
Flexural Strength | | ISO 178 | 60 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 560 | kg/cm²(MPa)[Lb/in²] |
Izod notch impact strength | | ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | | ISO 11359-2 | 1.3 | |
Deflection Temperature Under Load? | -,0.45Mpa | ISO 75-2 | 95 | °C |
Deflection Temperature Under Load? | -,1.8Mpa | ISO 75-2 | 45 | °C |
Melting Temperature | | | 176-180 | ℃(℉) |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 10 | mm/mm.℃ |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC 60093 | 10 | Ω.cm |
Volume Resistivity | | ASTM D257/IEC 60093 | 10^15 | Ω.cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.