Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | | | 0.20到0.80 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.10 | % |
Melt Mass-Flow Rate | 200°C/5.0kg | ISO1133 | 7.0 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO527-2/5 | 27.0 | Mpa |
Tensile Strain | Break | ISO527-2/5 | 40 | % |
Flexural Modulus | | ISO178 | 1500 | Mpa |
Flexural Stress | | ISO178 | 34.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 62.0 | °C |
Vicat Softening Temperature | | ISO306/A50 | 81.0 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO179 | 无断裂 | |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale | ISO2039-2 | 10 | |
Shore Hardness | Shore D | ISO868 | 68 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Haze | 2000µm | ISO3537 | 1.2 | % |
Transmittance | 2000µm | ISO3537 | 88.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.