Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 1.1 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.50 | % |
Moisture Absorption | 23°C,24hr,2.00mm | ISO62 | 0.40 | % |
Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % |
Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 13.5 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2 | 95.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 3.3 | % |
Tensile Modulus | | ISO527-2 | 5000 | Mpa |
Flexural Stress | | ISO178 | 143 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting Temperature | | ISO11357-3 | 225 | °C |
0.45MPa, Unannealed | | ISO75-2/B | 220 | °C |
1.8MPa, Unannealed | | ISO75-2/A | 200 | °C |
Glass Transition Temperature | | ISO11357-2 | 65.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | | IEC60112 | 575 | V |
Dielectric Strength | | IEC60243-1 | 35 | KV/mm |
Dissipation Factor? | 100Hz | IEC60250 | 0.010 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.010 | |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 250°C,1000sec^-1 | ISO11443 | 175 | Pa·s |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 57 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ISO4589-2 | 20 | % |
Burning Rate | 1.00mm | ISO3795 | 32 | mm/min |
Flammability level | 1.50mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.