PBT VALOX™ ENH4550-1001 SABIC INNOVATIVE SHANGHAI
95
- Unit Price:
- $4403 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 33MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity high strength
- Application Areas:Home appliance components Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| Shrinkage rate | MD：--2 | 内部方法 | 0.10to0.50 | % |
| MD：3.20mm | 内部方法 | 0.10to0.50 | % | |
| TD：--2 | 内部方法 | 0.60to1.2 | % | |
| TD：3.20mm | 内部方法 | 0.50to1.1 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.23 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.060 | % | |
| MeltViscosity | 250°C,1500sec^-1 | ISO11443 | 210 | Pa·s |
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 27 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2/5 | 112 | Mpa |
| Tensile strength 4 | Break | ASTMD638 | 105 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 112 | Mpa |
| Elongation rate 4 | Yield | ASTMD638 | 2.0 | % |
| Tensile strain | Yield | ISO527-2/5 | 2.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 2.0 | % |
| Tensile strain | Break | ISO527-2/5 | 2.0 | % |
| Bending modulus 5 | 50.0mmSpan | ASTMD790 | 9100 | Mpa |
| Bending modulus 6 | ISO178 | 9400 | Mpa | |
| Bending strength 6,7 | ISO178 | 170 | Mpa | |
| FlexuralStrength5 | Yield,50.0mmSpan | ASTMD790 | 161 | Mpa |
| Fracture bending strain 8 | ISO178 | 2.0 | % | |
| Tensile modulus 3 | ASTMD638 | 9900 | Mpa | |
| Tensile modulus | ISO527-2/1 | 10400 | Mpa | |
| Tensile strength 4 | Yield | ASTMD638 | 105 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ASTMD152513 | 202 | °C |
| -- | ISO306/A50 | 219 | °C | |
| -- | ISO306/B50 | 206 | °C | |
| -- | ISO306/B120 | 206 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.7E-05 | cm/cm/°C |
| MD：-40to150°C | ASTME831 | 2.2E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 3E-05 | cm/cm/°C | |
| MD：23to80°C | ISO11359-2 | 2.2E-05 | cm/cm/°C | |
| Vicat softening temperature | -- | ASTMD152512 | 215 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 216 | °C |
| Hot deformation temperature 11 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 219 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 204 | °C |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 201 | °C |
| RTIStr | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | UL746 | 140 | °C | |
| RTIElec | UL746 | 130 | °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO11359-2 | 9.1E-05 | cm/cm/°C |
| TD：-40to40°C | ISO11359-2 | 7.6E-05 | cm/cm/°C | |
| TD：-40to150°C | ASTME831 | 7.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 21 | KV/mm |
| Volume resistivity | IEC60093 | 1.0E+15to1.0E+16 | ohms·cm | |
| ASTMD257 | 1.0E+15to1.0E+16 | ohms·cm | ||
| Dielectric strength | 3.20mm,in Oil | ASTMD149 | 21 | KV/mm |
| Arc resistance 14 | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Leakage Trace Index | IEC60112 | 300 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC0 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 10 | 23°C | ISO180/1A | 7.0 | kJ/m² |
| Unscented Izod Impact Strength 10 | -30°C | ISO180/1U | 29 | kJ/m² |
| 23°C | ISO180/1U | 33 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 6.50 | J |
| Impact strength of simply supported beam without notch | -30°C | ISO179/2U | 33 | kJ/m² |
| 23°C | ISO179/2U | 36 | kJ/m² | |
| Suspended wall beam gap impact strength 10 | -30°C | ISO180/1A | 7.0 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 0.8mm | IEC60695-2-13 | 775 | °C |
| 3.0mm15 | IEC60695-2-13 | 775 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.