Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ISO294-4 | 0.40 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.40 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
Viscosity Number | | ISO307 | 105 | cm³/g |
Modeling Shrinkage | free,longitudinal | | 0.21 | % |
Modeling Shrinkage | free,transverse | | 1.1 | % |
Density / Specific Gravity | | ISO1183 | 1.47 | g/cm³ |
Apparent Density | | | 0.70到0.80 | g/cm³ |
Melt Volume flow Rate | 275°C/2.16kg | ISO1133 | 22.0 | cm3/10min |
Modeling Shrinkage | TD | ISO294-4 | 0.90 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | | ISO178 | 7010 | Mpa |
Flexural Stress | | ISO178 | 190 | Mpa |
Tensile Modulus | | ISO527-2 | 7500 | Mpa |
Tensile Stress | Break | ISO527-2 | 120 | Mpa |
Tensile Strain | Break | ISO527-2 | 2.8 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Maximum Service Temperature (short cycle operation) | | | 210 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 215 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 180 | °C |
Melting temperature | | ISO11357-3 | 223 | °C |
Linear thermal expansion coefficient | MD:23to80°C | ISO11359-2 | 2.0E-5到3.0E-5 | cm/cm/°C |
Specific Heat | | | 1100 | J/kg/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
Relative Permittivity | 100Hz | IEC60250 | 3.70 | |
Relative Permittivity | 1MHz | IEC60250 | 3.50 | |
Dissipation Factor? | 100Hz | IEC60250 | 1.4E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.018 | |
Comparative Tracking Index | SolutionA | IEC60112 | 300 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.5 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 40 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 40 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | H358/30 | ISO2039-1 | 190 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flammability level | 0.75mm | IEC60695-11-10,-20 | HB | |
Flammability level | 1.6mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.