PBT VALOX™ 357X-7001 SABIC INNOVATIVE US
99
- Unit Price:
- $4748 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 38MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant UV resistance
- Application Areas:Electrical appliances Electronic display Household goods Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 9.6 | g/10min |
| 265°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| 266°C/5.0kg | ASTMD1238 | 13 | g/10min | |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 8.00 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 10.0 | cm3/10min | |
| Shrinkage rate | MD1 | 内部方法 | 1.1到1.8 | % |
| MD:3.20mm | 内部方法 | 1.0到1.4 | % | |
| TD2 | 内部方法 | 0.90到1.8 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.50 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --3 | ASTMD638 | 2000 | Mpa | |
| Surrender 4 | ASTMD638 | 50.0 | Mpa | |
| yield | ISO527-2/50 | 50.0 | Mpa | |
| Fracture 5 | ASTMD638 | 40.0 | Mpa | |
| crack | ISO527-2/50 | 40.0 | Mpa | |
| Surrender 6 | ASTMD638 | 5.0 | % | |
| yield | ISO527-2/50 | 5.0 | % | |
| Fracture 7 | ASTMD638 | 30 | % | |
| crack | ISO527-2/50 | 30 | % | |
| 50.0mm span 8 | ASTMD790 | 2100 | Mpa | |
| --9 | ISO178 | 2000 | Mpa | |
| --10 | ISO178 | 80.0 | Mpa | |
| Yield, 50.0mm span 11 | ASTMD790 | 78.0 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 33.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTI | UL746 | 140 | °C | |
| -- | ASTMD1525,ISO306/B501322 | 145 | °C | |
| ASTMD1525,ISO306/A501423 | 180 | °C | ||
| ISO306/B120 | 150 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 9.2E-05 | cm/cm/°C | |
| Flow: 23 to 80 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 8.4E-05 | cm/cm/°C | |
| Horizontal: 23 to 80 ° C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.17 | W/m/K | |
| RTIElec | UL746 | 120 | °C | |
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 130 | °C | |
| 0.45MPa, unannealed, 100mm span 18 | ISO75-2/Be | 135 | °C | |
| 0.45MPa, unannealed, 64.0mm span 19 | ISO75-2/Bf | 130 | °C | |
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 85.0 | °C | |
| 1.8MPa, unannealed, 100mm span 20 | ISO75-2/Ae | 85.0 | °C | |
| 1.8MPa, unannealed, 64.0mm span 21 | ISO75-2/Af | 85.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 50Hz | IEC60250 | 3.00 | ||
| 60Hz | IEC60250 | 3.00 | ||
| 1MHz | ASTMD150 | 0.013 | ||
| 50Hz | IEC60250 | 2E-03 | ||
| 60Hz | IEC60250 | 2E-03 | ||
| 1MHz | IEC60250 | 1.3E-03 | ||
| Arc resistance 24 | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Leakage Trace Index | -- | IEC60112 | 225 | V |
| SolutionB | IEC60112 | 100 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Hot wire ignition | HWI | UL746 | PLC3 | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257,IEC60093 | >1.0E+15 | ohms·cm | |
| 1.60mm,inOil | ASTMD149 | 25 | KV/mm | |
| 3.20mm, inoil | ASTMD149 | 17 | KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 34 | KV/mm | |
| 1.60mm, in oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm, in oil | IEC60243-1 | 17 | KV/mm | |
| 1MHz | ASTMD150,IEC60250 | 3.00 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 310 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23°C17 | ISO180/1A | 40 | kJ/m² | |
| Cantilever beam without notch impact strength | -30°C | ASTMD4812,ISO180/1U | 无断裂 | |
| 23°C | ASTMD4812,ISO180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 35.0 | J |
| -30°C12 | ISO179/1eA,ISO179/2C | 20 | kJ/m² | |
| 23°C13 | ISO179/1eA | 45 | kJ/m² | |
| 23°C | ISO179/2C | 40 | kJ/m² | |
| Simply supported beam without notch impact strength 14 | -30°C | ISO179/1eU,ISO179/2U | 无断裂 | |
| 23°C | ISO179/1eU,ISO179/2U | 无断裂 | ||
| -30°C | ASTMD256 | 150 | J/m | |
| 0°C | ASTMD256 | 190 | J/m | |
| 23°C | ASTMD256 | 500 | J/m | |
| -30°C15 | ISO180/1A | 10 | kJ/m² | |
| 0°C16 | ISO180/1A | 20 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 115 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 115 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.750mm | UL94 | V-0 | |
| 2.50mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.00mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO4589-2 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.