Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 1.9 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.9 | % |
Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 10 | g/10min |
Ejection Temperature | | | 170 | °C |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | | ISO527-2 | >50 | % |
Flexural Stress | | ISO178 | 85.0 | Mpa |
Tensile Stress | Yield | ISO527-2 | 57.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 4.0 | % |
Tensile Modulus | | ISO527-2 | 2600 | Mpa |
Tensile Modulus | 0.00 mm, 23 ℃, Injection Molded | MPa | ISO 527-1, -2 | 2600 |
Flexural Strength | 0.00 mm, 23 ℃, 0.0 % | MPa | ISO 178 | 85 |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | -,1.50 mm | | UL94 | HB |
Flame Rating | -,3.00 mm | | UL94 | HB |
Melting Temperature | | ISO11357-3 | 225 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC60243-1 | 39 | KV/mm |
Dissipation Factor? | 100Hz | IEC60250 | 5E-04 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.019 | |
Surface Resistivity | | IEC60093 | 1E+14 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Relative Permittivity | 100Hz | IEC60250 | 3.40 | |
Relative Permittivity | 1MHz | IEC60250 | 3.30 | |
Comparative Tracking Index | | IEC60112 | 400 | V |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | HB | |
UL flame retardant rating | 3.0mm | UL94 | HB | |
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB | |
Oxygen Index | | ISO4589-2 | 21 | % |
FMVSS Flammability | | FMVSS302 | SE | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
EmissionofOrganicCompounds | | VDA277 | 145 | µgC/g |
Odor | | VDA270 | 3.00 | |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | % | ISO 4589-1, -2 | 21 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.