PBT VALOX™ ENH4530 SABIC INNOVATIVE NANSHA
41
- Unit Price:
- $4035 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD1 | 内部方法 | 0.30到0.80 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.15 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.070 | % | |
| Melt Mass-Flow Rate | 265°C/5.0kg | ASTMD1238 | 24 | g/10min |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 17.0 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 18.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| yield | ISO527-2/5 | 80.0 | Mpa | |
| ISO527-2/5 | 2.0 | % | ||
| fracture | ISO527-2/5 | 3.0 | % | |
| ISO527-2/5 | 80.0 | Mpa | ||
| --8 | ISO178 | 6400 | Mpa | |
| --9 | ISO178 | 130 | Mpa | |
| Break | ASTMD638 | 80.0 | Mpa | |
| --2 | ASTMD638 | 7300 | Mpa | |
| Yield | ASTMD638 | 80.0 | Mpa | |
| Break | ASTMD638 | 3.0 | % | |
| 50.0mm Span | ASTMD790 | 5800 | Mpa | |
| Yield,50.0mm Span | ASTMD790 | 120 | Mpa | |
| Yield | ASTMD638 | 2.0 | % | |
| Break,50.0mm Span | ASTMD790 | 120 | Mpa | |
| Flexural Strain (Break) | ISO178 | 3.0 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 220 | °C | |
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 200 | °C | |
| RTIElec | UL746 | 140 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 200 | °C | |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 220 | °C | |
| -- | ASTMD1525,ISO306/B50,ISO306/B12020 | 205 | °C | |
| ASTMD152521 | 217 | °C | ||
| ISO306/A50 | 220 | °C | ||
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| RTI | UL746 | 140 | °C | |
| Linear thermal expansion coefficient | MD:-40to40°C | ISO11359-2 | 2.9E-05 | cm/cm/°C |
| MD:23to150°C | ISO11359-2 | 4.2E-05 | cm/cm/°C | |
| TD:-40to40°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD:23to150°C | ISO11359-2 | 1.7E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| Dielectric Constant | 1MHz | ASTMD150,IEC60250 | 3.70 | |
| Volume Resistivity | ASTMD257,IEC60093 | 1E+15 | ohms·cm | |
| Dissipation Factor? | 1MHz | ASTMD150,IEC60250 | 0.15 | |
| 0.800mm,inOil | ASTMD149 | 28 | KV/mm | |
| 1.60mm,inOil | ASTMD149 | 21 | KV/mm | |
| 3.20mm,inOil | ASTMD149 | 17 | KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 28 | KV/mm | |
| 1.60mm,in Oil | IEC60243-1 | 21 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Fill Analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 150 | Pa·s |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/2U | 25 | kJ/m² |
| 23°C | ISO179/2U | 35 | kJ/m² | |
| 23°C17 | ISO180/1U | 30 | kJ/m² | |
| 23°C | ASTMD4812 | 400 | J/m | |
| ASTMD256 | 50 | J/m | ||
| -30°C | ASTMD4812 | 360 | J/m | |
| ASTMD256 | 50 | J/m | ||
| 0°C | ASTMD256 | 50 | J/m | |
| -30°C13 | ISO180/1A | 6.0 | kJ/m² | |
| 0°C14 | ISO180/1A | 6.0 | kJ/m² | |
| -30°C16 | ISO180/1U | 23 | kJ/m² | |
| 23°C15 | ISO180/1A | 6.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Sale | ISO2039-2 | 98 | |
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 128 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.800mm | UL94 | V-0 | |
| Glow Wire Flammability Index | 3.00mm | IEC60695-2-12 | 960 | °C |
| Glow Wire Ignition Temperature | 3.00mm | IEC60695-2-13 | 750 | °C |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filler Content | ASTMD229 | 15 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.