PBT VALOX™ 325FC-1001 SABIC INNOVATIVE SHANGHAI
101
- Unit Price:
- $3886 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Easy to process
- Application Areas:Electrical appliances Industrial applications Construction field Automotive External Parts Outdoor applications
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 20.0 | cm3/10min |
| 250°C/5.0kg | ISO1133 | 50.0 | cm3/10min | |
| Shrinkage rate | MD | 内部方法 | 2.0到2.6 | % |
| TD | 内部方法 | 0.90到1.8 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.34 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.080 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --2 | ASTMD638 | 2500 | Mpa | |
| Surrender 3 | ASTMD638 | 60.0 | Mpa | |
| yield | ISO527-2/50 | 60.0 | Mpa | |
| Fracture 4 | ASTMD638 | 60.0 | Mpa | |
| crack | ISO527-2/50 | 60.0 | Mpa | |
| Surrender 5 | ASTMD638 | 7.0 | % | |
| yield | ISO527-2/50 | 10 | % | |
| Fracture 6 | ASTMD638 | 15 | % | |
| crack | ISO527-2/50 | 15 | % | |
| Bending modulus 7 | ISO178 | 2400 | Mpa | |
| Bending stress 8 | ISO178 | 85.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0.45MPa, unannealed, 64.0mm span | ISO75-2/Bf | 150 | °C | |
| 1.8MPa, unannealed, 64.0mm span | ISO75-2/Af | 50.0 | °C | |
| -- | ASTMD1525,ISO306/B50,ISO306/B12014 | 185 | °C | |
| ASTMD1525,ISO306/A501015 | 220 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 165 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0°C10 | ISO180/1A | 4.0 | kJ/m² | |
| 23°C11 | ISO180/1A | 4.0 | kJ/m² | |
| -30°C | ASTMD4812 | 无断裂 | ||
| 23°C | ASTMD4812,ISO180/1U | 无断裂 | ||
| -30°C12 | ISO180/1U | 100 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/2U | 80 | kJ/m² |
| 23°C | ISO179/2U | 无断裂 | ||
| -30°C | ASTMD256 | 36 | J/m | |
| 0°C | ASTMD256 | 36 | J/m | |
| 23°C | ASTMD256 | 38 | J/m | |
| -30°C9 | ISO180/1A | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 117 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 145 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.