Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.00mm4 | 内部方法 | 0.40 | % |
Modeling Shrinkage | TD:3.00mm2 | 内部方法 | 0.90 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.070 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2 | 95.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 3.1 | % |
Tensile Modulus | 23°C | ISO527-2 | 6600 | Mpa |
Flexural Modulus | 23°C | ISO178 | 6300 | Mpa |
Flexural Stress | 23°C | ISO178 | 150 | Mpa |
Coefficient of Friction (vs.Metal) | | SuzukiMethod | 0.16 | |
Coefficient of Friction | | | 0.20 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:-30to100°C | ISO11359-2 | 5E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 207 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor | 23°C,50Hz | IEC60250 | 2E-03 | |
Dissipation Factor | 23°C,1MHz | IEC60250 | 0.020 | |
Dielectric Constant | 23°C,50Hz | IEC60250 | 3.80 | |
Dielectric Constant | 23°C,1kHz | IEC60250 | 3.80 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 57 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.6mm | UL94 | V-0 | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
BarFlowLength7 | 250°C,1.00mm | 内部方法 | 113 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.