PBT Cristin® SK608 BK509 DUPONT USA
40
- Unit Price:
- $3346 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 23.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Moisture Absorption | -,23C/59RH | % | ISO 62 | 0.1 |
-,Sat/23C | % | ISO 62 | 0.3 | |
Saturation,23°C,2.00mm | ISO62 | 0.30 | % | |
Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.10 | % | |
Modeling Shrinkage | -,Across Flow | % | ISO 294-4 | 1.3 |
-,Flow | % | ISO 294-4 | 0.3 | |
TD | ISO294-4 | 1.1 | % | |
MD | ISO294-4 | 0.30 | % | |
MediumDensity | 1.47 | g/cm³ | ||
Ejection Temperature | 170 | °C |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Flexural Stress | ISO178 | 210 | Mpa | |
Notched Impact Strength | 23 ℃, Type 1, Notch A | KJ/m | ISO 180 | |
Tensile Stress | Break | ISO527-2 | 140 | Mpa |
Tensile Strain | Break | ISO527-2 | 2.0 | % |
Tensile Modulus | ISO527-2 | 14200 | Mpa | |
23℃, 1.0 mm/min | MPa | ISO 527-1, -2 | 14300 | |
Flexural Modulus | ISO178 | 13300 | Mpa | |
Flexural Strength | 23℃ | MPa | ISO 178 | 235 |
Tensile Strain (Break) | 23℃ | % | ISO 527-1, -2 | 2.1 |
Tensile Stress (Break) | 23 ℃, 5 mm/min | MPa | ISO 527-1, -2 | 160 |
Charpy Notched Impact Strength | -,-30 ℃, Type 1, Edgewise | KJ/m | ISO 179 | |
-,23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | ||
Charpy Notched Impact Strength | 23 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Coefficient of Linear Thermal Expansion | 平行Flow ,23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | 0.000080 |
垂直Flow ,23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | 0.000080 | |
Melting Temperature | ISO11357-3 | 225 | °C | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 222 | °C |
1.8MPa,Unannealed | ISO75-2/A | 207 | °C | |
-,0.45 Mpa,Unannealed | ℃ | ISO 75B-1, -2 | ||
-,1.8 Mpa,Unannealed | ℃ | ISO 75A-1, -2 | 205 | |
Vicat Softening Temperature | ISO306/B50 | 215 | °C | |
Flame Rating | -,0.750 mm | UL 94 | HB | |
-,1.50 mm | UL 94 | HB | ||
-,3.00 mm | UL 94 | HB | ||
Linear thermal expansion coefficient | MD | ISO11359-2 | 2E-05 | cm/cm/°C |
TD | ISO11359-2 | 8E-05 | cm/cm/°C | |
Melting temperature | ℃ | ISO 3146 | 225 |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Dielectric Strength | IEC60243-1 | 32 | KV/mm | |
Relative Permittivity | 100Hz | IEC60250 | 4.10 | |
1MHz | IEC60250 | 3.90 | ||
Comparative Tracking Index | IEC60112 | 475 | V | |
Dissipation Factor? | 100Hz | IEC60250 | 3.8E-03 | |
1MHz | IEC60250 | 0.013 | ||
Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 65 | kJ/m² |
23°C | ISO179/1eU | 55 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
UL flame retardant rating | 0.75mm | UL94 | HB | |
1.5mm | UL94 | HB | ||
0.75mm | IEC60695-11-10,-20 | HB | ||
1.5mm | IEC60695-11-10,-20 | HB | ||
Oxygen Index | ISO4589-2 | 20 | % | |
FMVSS Flammability | FMVSS302 | B | ||
Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
EmissionofOrganicCompounds | VDA277 | 70.0 | µgC/g | |
Odor | VDA270 | 3.00 |
Other performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Oxygen Index | % | ISO 4589-1, -2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.