Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.78 | % |
Moisture Absorption | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.23 | % |
Modeling Shrinkage | TD | ISO294-4 | 0.80 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.40 | % |
MediumDensity | | | 1.36 | g/cm³ |
Ejection Temperature | | | 170 | °C |
SpecificHeatCapacityofMelt | | | 1900 | J/kg/°C |
ThermalConductivityofMelt | | | 0.25 | W/m/K |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Creep Modulus | 1hr | ISO899-1 | 7500 | Mpa |
Tensile Creep Modulus | 1000hr | ISO899-1 | 6000 | Mpa |
Flexural Stress | | ISO178 | 155 | Mpa |
Tensile Stress | Break | ISO527-2 | 110 | Mpa |
Tensile Strain | Break | ISO527-2 | 2.0 | % |
Tensile Modulus | | ISO527-2 | 8500 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 215 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 175 | °C |
Melting Temperature | | ISO11357-3 | 225 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 3E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 1E-04 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 100Hz | IEC60250 | 3.70 | |
Relative Permittivity | 1MHz | IEC60250 | 3.50 | |
Comparative Tracking Index | | IEC60112 | 300 | V |
Surface Resistivity | | IEC60093 | 1E+14 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Dielectric Strength | -- | IEC60243-1 | 29 | KV/mm |
Dielectric Strength | 1.00mm3 | IEC60243-1 | 29 | KV/mm |
Dielectric Strength | 2.00mm4 | IEC60243-1 | 20 | KV/mm |
Dielectric Strength | 2.00mm3 | IEC60243-1 | 20 | KV/mm |
Dissipation Factor? | 100Hz | IEC60250 | 1.8E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.015 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | -30°C | ISO180/1U | 33 | kJ/m² |
Notched Izod impact strength | 23°C | ISO180/1U | 33 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 35 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 40 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
UL flame retardant rating | 3.0mm | UL94 | V-0 | |
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | V-0 | |
UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | V-0 | |
Oxygen Index | | ISO4589-2 | 27 | % |
FMVSS Flammability | | FMVSS302 | DNI | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.