PBT Cristin® HR5315 DUPONT USA
79
- Unit Price:
- $3372 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance Glass fiber reinforced Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Electronic and electrical
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | -，Across Flow | % | ISO 294-4 | 1.1 |
| -，Flow | % | ISO 294-4 | 0.5 | |
| TD | ISO294-4 | 1.1 | % | |
| MD | ISO294-4 | 0.50 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| MediumDensity | 1.14 | g/cm³ | ||
| Ejection Temperature | 170 | °C | ||
| SpecificHeatCapacityofMelt | 1860 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K | ||
| Viscosity number | ISO307 | 95.0 | cm³/g | |
| FlowLength2 | 2.00mm | 430 | mm |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | -，-40 ℃, Type 1 | kJ/m² | ISO 180 | |
| -，23 ℃, Type 1 | kJ/m² | ISO 180 | 45 | |
| Tensile Creep Modulus | 1hr | ISO899-1 | 5000 | Mpa |
| Tensile Strain (Break) | 23℃ | % | ISO 527-1, -2 | 3 |
| Tensile Stress (Break) | 23℃ | MPa | ISO 527-1, -2 | |
| Flexural Stress | ISO178 | 150 | Mpa | |
| Tensile Stress | Break | ISO527-2 | 95.0 | Mpa |
| Tensile Strain | Break | ISO527-2 | 3.0 | % |
| Notched Impact Strength | -，-40 ℃, Type 1, Notch A | kJ/m² | ISO 180 | |
| -，23 ℃, Type 1, Notch A | kJ/m² | ISO 180 | ||
| Tensile Creep Modulus | 1000hr | ISO899-1 | 4200 | Mpa |
| Tensile Modulus | 23℃ | MPa | ISO 527-1, -2 | 5200 |
| ISO527-2 | 5200 | Mpa | ||
| Flexural Modulus | 23℃ | MPa | ISO 178 | 4500 |
| ISO178 | 4700 | Mpa | ||
| Flexural Strength | 23℃ | MPa | ISO 178 | 140 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | |
| -，1.80 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | ||
| 0.45MPa,Unannealed | ISO75-2/B | 220 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 200 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 4.1E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Melting Temperature | ISO11357-3 | 225 | °C | |
| Glass Transition Temperature | ISO11357-2 | 65.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.80 | |
| 1MHz | IEC60250 | 3.60 | ||
| Comparative Tracking Index | IEC60112 | 350 | V | |
| Dissipation Factor? | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.010 | ||
| Dielectric Strength | IEC60243-1 | 42 | KV/mm | |
| Surface Resistivity | IEC60093 | 1E+13 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 30 | kJ/m² |
| 23°C | ISO179/1eU | 60 | kJ/m² | |
| Notched Izod impact strength | -40°C | ISO180/1U | 30 | kJ/m² |
| -30°C | ISO180/1U | 40 | kJ/m² | |
| 23°C | ISO180/1U | 45 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R-Scale | ISO2039-2 | 115 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ISO4589-2 | 20 | % | |
| FMVSS Flammability | FMVSS302 | B | ||
| Burning Rate | 1.00mm | ISO3795 | <100 | mm/min |
| Flammability level | 1.5mm | IEC60695-11-10,-20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.