PBT CELANEX® 2300GV3/20 CELANESE USA

Unit Price:
$4213 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.20	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.15	%
Modeling Shrinkage	TD	ISO294-4	1.0到1.3	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.40到0.50	%
Melt Volume flow Rate	250°C/2.16kg	ISO1133	14.0	cm3/10min
Melt Volume flow Rate	Melt Volume flow Rate	250°C/2.16kg	ISO1133	20.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Creep Modulus	1hr	ISO899-1	6200	Mpa
	Tensile Creep Modulus	1000hr	ISO899-1	4800	Mpa
		Tensile Creep Modulus	1hr	ISO899-1	3500	Mpa
		Tensile Creep Modulus	Tensile Creep Modulus	1000hr	ISO899-1	2400	Mpa
Flexural Stress	23°C	ISO178	86.0	Mpa
Flexural Stress	Flexural Stress	23°C	ISO178	170	Mpa
Tensile Stress	Break	ISO527-2/1A/5	50.0	Mpa
Tensile Stress	Tensile Stress	Break	ISO527-2/1A/5	125	Mpa
Tensile Strain	Break	ISO527-2/1A/5	3.0	%
Tensile Strain	Tensile Strain	Break	ISO527-2/1A/5	4.0	%
Tensile Modulus		ISO527-2/1A/1	3500	Mpa
Tensile Modulus	Tensile Modulus		ISO527-2/1A/1	7400	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	220	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	195	°C
		Deflection Temperature Under Load?	8.0MPa,Unannealed	ISO75-2/C	100	°C
			Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	180	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	70.0	°C
Melting Temperature		ISO11357-3	225	°C
Vicat Softening Temperature		ISO306/B50	190	°C
Vicat Softening Temperature	Vicat Softening Temperature		ISO306/B50	215	°C
Linear thermal expansion coefficient	MD	ISO11359-2	3.5E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	MD	ISO11359-2	1.1E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Dielectric Strength		IEC60243-1	31	KV/mm
Dielectric Strength	Dielectric Strength		IEC60243-1	26	KV/mm
Relative Permittivity	100Hz	IEC60250	4.40
	Relative Permittivity	1MHz	IEC60250	4.20
		Relative Permittivity	100Hz	IEC60250	4.20
		Relative Permittivity	Relative Permittivity	1MHz	IEC60250	4.10
Comparative Tracking Index		IEC60112	225	V
Comparative Tracking Index	Comparative Tracking Index		IEC60112	350	V
Dissipation Factor?	100Hz	IEC60250	1.6E-03
	Dissipation Factor?	1MHz	IEC60250	0.019
		Dissipation Factor?	100Hz	IEC60250	8.5E-03
		Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.018

Fill Analysis	Test Method	Test Result	Unit
SpecificHeatCapacityofMelt	内部方法	1840	J/kg/°C
ThermalConductivityofMelt	内部方法	0.16	W/m/K
DensityofMelt	内部方法	1.230	g/cm³

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	34	kJ/m²
	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	34	kJ/m²
		Charpy Unnotched Impact Strength	23°C	ISO179/1eU	46	kJ/m²
		Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	43	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.2mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.8mm	UL94	HB
		UL flame retardant rating	UL flame retardant rating	1.6mm	UL94	HB
Oxygen Index		ISO4589-2	21	%
Oxygen Index	Oxygen Index		ISO4589-2	20	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.