PBT Cristin® CE2055 NC010 DUPONT USA

Unit Price:
$3588 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
32MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.31

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt index	250°C/2.16 kg, Procedure A	g/10min	ISO 1133
Modeling Shrinkage	MD2.0mm	ISO294-4	1.80	%
Modeling Shrinkage	Modeling Shrinkage	TD2.0mm	ISO294-4	2.00	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179/1eA	3.5	kJ/m²
Notched Izod Impact Strength	23°C	ISO180/1A	3.9	kJ/m²
Tensile Elongation?(Break)	23°C	ISO527-2	13	%
Tensile Modulus	23°C	ISO527-2	2600	Mpa
	Tensile Modulus	0.00 mm, 23 ℃, Injection Molded	MPa	ISO 527-1, -2	2600
	Tensile Modulus	Tensile Modulus		ASTM D638/ISO 527	2600	kg/cm²(MPa)[Lb/in²]
Tensile Strength	23°C	ISO527-2	60.0	Mpa
Flexural Strength		ASTM D790/ISO 178	82	kg/cm²(MPa)[Lb/in²]
	Flexural Strength	0.00 mm, 23 ℃, 0.0 %	MPa	ISO 178	82
	Flexural Strength	Flexural Strength	23°C	ISO178	82.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPaAnnealed	ISO75-2/B	184	°C
	Deflection Temperature Under Load?	0.45MPaUnannealed	ISO75-2/Bf	150	°C
		Deflection Temperature Under Load?	1.80MPaAnnealed	ISO75-2/A	73	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.80MPaAnnealed	ISO75-2/Af	55	°C
Vicat Softening Temperature		ISO306/B50	175	°C
Vicat Softening Temperature	Vicat Softening Temperature	Melting Temperature	ISO11357-3	225	°C

Processing	Test Condition	Test Method	Test Result	Unit
Mold Temperature			30-130	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.