Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.70 | % |
Modeling Shrinkage | TD2.0mm | ISO294-4 | 1.20 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.40 | % |
Moisture Absorption | 23°C,50RH | ISO62 | 0.20 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 40 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 40 | kJ/m² |
Unnotched Izod Impact Strength | 23°C | ISO180/1U | 27 | kJ/m² |
Unnotched Izod Impact Strength | -30°C | ISO180/1U | 26 | kJ/m² |
Tensile Creep Modulus | 1Hr | ISO899-1 | 4000 | Mpa |
Tensile Creep Modulus | 1000Hr | ISO899-1 | 2500 | Mpa |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.00 | kJ/m² |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 6.00 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 4.50 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/1A | 5.00 | kJ/m² |
Tensile Elongation?(Break) | 23°C | ISO527-2 | 4.70 | % |
Tensile Modulus | 23°C | ISO527-2 | 4500 | Mpa |
Tensile Strength | 23°C | ISO527-2 | 90 | Mpa |
Flexural Strength | 23°C | ISO178 | 140 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPaUnannealed | ISO75-2/Bf | 215 | °C |
Deflection Temperature Under Load? | 1.80MPaUnannealed | ISO75-2/Af | 175 | °C |
Vicat Softening Temperature | | ISO306/B50 | 205 | °C |
Melting temperature | | ISO11357-3 | 225 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 6E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Insulation strength | | IEC60243-1 | 35 | KV/mm |
Volume Resistivity | | IEC60093 | 1E+16 | Ω.cm |
Comparative Tracking Index | | IEC60112 | 300 | V |
Dissipation Factor? | 23°C | IEC60250 | 2E-03 | 100HZ |
Dissipation Factor? | 23°C | IEC60250 | 0.020 | 1MHz |
Dielectric Constant | 23°C | IEC60250 | 3.90 | 100HZ |
Dielectric Constant | 23°C | IEC60250 | 3.50 | 1MHz |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Oxygen Index | | ISO4589-2 | 20 | % |
Fire rating | Allcolor | UL-94 | 0.75mm | |
Fire rating | Allcolor | UL-94 | 1.50mm | HB |
Fire rating | Allcolor | UL-94 | 3.00mm | HB |
Fire rating | Allcolor | UL-94 | 6.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.