PBT Cristin® BM6450XD BK560 DUPONT USA

Unit Price:
$3675 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:Blow molding applications
Color:--
Grade:Extrusion grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.21

Physical Properties	Test Condition	Test Method	Test Result	Unit
MediumDensity			1.03	g/cm³
SpecificHeatCapacityofMelt			2210	J/kg/°C
ThermalConductivityofMelt			0.15	W/m/K
Modeling Shrinkage	TD	ISO294-4	1.7	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.5	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Notched Impact Strength	23 ℃, Type 1, Notch A	KJ/m	ISO 180
Charpy Unnotched Impact Strength	-，-30 ℃, Type 1, Edgewise	KJ/m	ISO 179	No Break
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	-，23 ℃, Type 1, Edgewise	KJ/m	ISO 179	No Break
Tensile Stress	Yield	ISO527-2	34.0	Mpa
Tensile Strain	Yield	ISO527-2	9.0	%
Tensile Modulus		ISO527-2	1600	Mpa
	Tensile Modulus	23 ℃, 1.0 mm/min	MPa	ISO 527-1, -2	1600
	Tensile Modulus	Tensile Modulus		ASTM D638/ISO 527	1600	kg/cm²(MPa)[Lb/in²]
Flexural Modulus		ASTM D790/ISO 178	1600	kg/cm²(MPa)[Lb/in²]
	Flexural Modulus	23℃, 2 mm/min	MPa	ISO 178	1600
	Flexural Modulus	Flexural Modulus		ISO178	1600	Mpa
Flexural Strength	23℃	MPa	ISO 178
Flexural Strength	Flexural Strength		ASTM D790/ISO 178	50	kg/cm²(MPa)[Lb/in²]
Tensile Stress (Yield)	23 ℃, 50 mm/min	MPa	ISO 527-1, -2	34
Tensile Strain (Yield)	23 °C, 50 mm/min	%	ISO 527-1, -2	9.3
Tensile Strain (Break)	23 °C, 50 mm/min	%	ISO 527-1, -2
Nominal Tensile Strain at Break		ISO527-2	>50	%
Charpy Notched Impact Strength	23 ℃, Type 1, Edgewise, Notch A	KJ/m	ISO 179
Flexural Stress		ISO178	50.0	Mpa
Tensile Strain (Break)	23 ℃, 50 mm/min	%	ISO 527-1, -2

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Melting temperature		℃	ISO 3146
Melting Temperature		ISO11357-3	220	°C
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	80.0	°C
	Deflection Temperature Under Load?	0.45MPa,Annealed	ISO75-2/B	130	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	50.0	°C
			Deflection Temperature Under Load?	-，0.45 Mpa，Unannealed（Flatwise）	℃	ISO 75B-1, -2	130
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	-，1.80 Mpa，Unannealed（Flatwise）	℃	ISO 75B-1, -2

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC60243-1	31	KV/mm
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Dissipation Factor?	100Hz	IEC60250	7E-03
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.020

Processing	Test Condition	Test Method	Test Result	Unit
Mold Temperature			30-130	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak

Flammability	Test Condition	Test Method	Test Result	Unit
FMVSS Flammability		FMVSS302	B
Burning Rate	1.00mm	ISO3795	40	mm/min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.