Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant UV resistance
Application Areas:Electrical appliances Electronic display Household goods switch Shell Spool Lighting fixtures
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD：--3	内部方法	1.2to1.6	%
Water absorption rate	24hr	ASTMD570	0.080	%
	Water absorption rate	Saturation,23°C	ISO62	0.50	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.15	%
Outdoor applicability		UL746C	f2
Density/specific gravity		ASTMD792	1.35	g/cm³
Specific volume		ASTMD792	0.740	cm³/g
Density/specific gravity		ISO1183	1.34	g/cm³
Melt mass flow rate	250°C/5.0kg	ASTMD1238	9.6	g/10min
Melt volume flow rate	250°C/5.0kg	ISO1133	8.00	cm3/10min
Shrinkage rate	MD：--2	内部方法	0.80to1.1	%
	Shrinkage rate	MD：--3	内部方法	1.0to1.4	%
		Shrinkage rate	MD：3.20mm	内部方法	1.0to1.4	%
		Shrinkage rate	Shrinkage rate	TD：--2	内部方法	0.90to1.3	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus 4		ASTMD638	2020	Mpa
Tensile modulus		ISO527-2/1	2200	Mpa
Tensile strength 6	Yield	ASTMD638	48.0	Mpa
Tensile stress	Yield	ISO527-2/50	50.0	Mpa
Tensile strength 5	Break	ASTMD638	42.0	Mpa
Tensile stress	Break	ISO527-2/50	40.0	Mpa
Tensile strain 5	Yield	ASTMD638	5.0	%
Tensile strain	Yield	ISO527-2/50	5.0	%
Tensile strain 5	Break	ASTMD638	54	%
Tensile strain	Break	ISO527-2/50	30	%
Bending modulus 7	50.0mmSpan	ASTMD790	2100	Mpa
Bending modulus 7	Bending modulus 7		ISO178	2000	Mpa
Bending strength 7,8		ISO178	73.0	Mpa
Bending strength 7	Yield,50.0mmSpan	ASTMD790	78.0	Mpa
FlexuralStrength6	Break,50.0mmSpan	ASTMD790	78.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	1.2E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO11359-2	7.2E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8.4E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO11359-2	8.4E-05	cm/cm/°C
RTIElec		UL746	120	°C
Evolution Calendar intelligent importer		UL746	120	°C
RTIStr		UL746	140	°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTMD648	135	°C
	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTMD648	138	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTMD648	98.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTMD648	99.0	°C
Hot deformation temperature 12	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	84.0	°C
Vicat softening temperature		ASTMD152513	134	°C
	Vicat softening temperature	--	ISO306/B50	145	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	150	°C
BallPressureTest14	125°C	IEC60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.2E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	3.20mm,in Oil	ASTMD149	19	KV/mm
Dielectric constant	100Hz	ASTMD150	3.20
Dielectric constant	Dielectric constant	1MHz	ASTMD150	3.20
Dissipation factor	100Hz	ASTMD150	3E-03
Dissipation factor	Dissipation factor	1MHz	ASTMD150	0.030
Arc resistance 15		ASTMD495	PLC6
Compared to the anti leakage trace index	CTI	UL746	PLC2
High arc combustion index	HAI	UL746	PLC3
High voltage arc tracing rate	HVTR	UL746	PLC3
Hot wire ignition	HWI	UL746	PLC2
Volume resistivity		ASTMD257	>1.2E+16	ohms·cm
Dielectric strength	1.60mm,in Oil	ASTMD149	25	KV/mm
Dielectric strength	Dielectric strength	3.20mm,inAir	ASTMD149	19	KV/mm

Impact performance	Test Condition	Test Method	Test Result	Unit
CharpyNotchedImpactStrength9	23°C	ISO179/1eA	45	kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTMD256	150	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTMD256	320	J/m
Suspended wall beam gap impact strength 10	-30°C	ISO180/1A	10	kJ/m²
Suspended wall beam gap impact strength 10	Suspended wall beam gap impact strength 10	23°C	ISO180/1A	45	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTMD4812	NoBreak
Dart impact equipped with measuring instruments	23°C,TotalEnergy	ASTMD3763	35.8	J
Falling hammer impact	23°C	ASTMD3029	43.4	J
Falling hammer impact	Falling hammer impact	23°C11	ASTMD3029	43.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	117

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.46mm	UL94	HB
	UL flame retardant rating	0.63mm	UL94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA
Burning wire flammability index	1.0mm	IEC60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC60695-2-13	775	°C
	Hot filament ignition temperature	2.0mm	IEC60695-2-13	750	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC60695-2-13	725	°C
Extreme Oxygen Index		ASTMD2863	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.