PBT CELANEX® 3201 CELANESE USA

Unit Price:
$4192 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density / Specific Gravity		ASTMD792	1.41	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.42	g/cm³
Melt Volume flow Rate	250°C/2.16kg	ISO1133	17.0	cm3/10min
Modeling Shrinkage	MD	ASTMD955	0.50to0.70	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.50to0.70	%
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.20	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ISO527-2/1A/1	6000	Mpa
Tensile Strength	Break,23°C	ASTMD638	93.1	Mpa
Tensile Stress	Break	ISO527-2/1A/5	100	Mpa
Tensile Elongation	Break,23°C	ASTMD638	3.0	%
Tensile Strain	Break	ISO527-2/1A/5	3.5	%
Flexural Modulus	23°C	ISO178	5600	Mpa
Flexural Stress	23°C	ISO178	160	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	213	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	218	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	192	°C
		Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	195	°C
Glass Transition Temperature		ISO11357-2	60.0	°C
Vicat Softening Temperature		ISO306/B50	220	°C
Peak Melting Temperature		ASTMD3418	225	°C
Melting Temperature		ISO11357-3	225	°C
Linear thermal expansion coefficient	MD	ISO11359-2	3.5E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume Resistivity		ASTMD257	1E+15	ohms·cm
Dielectric Strength		ASTMD149	18	KV/mm
Dielectric Constant	1kHz	ASTMD150	3.50

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	23°C	ISO179/1eA	6.5	kJ/m²
Notched Izod Impact Strength	-30°C	ISO180/1A	7.0	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	7.0	kJ/m²

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	--	UL94	HB
UL flame retardant rating	UL flame retardant rating	0.9mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.