PBT CELANEX® 3300D CELANESE USA
90
- Unit Price:
- $2987 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Automotive sector currency
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.20 | % |
| Flow | ASTMD955 | 0.30到0.50 | % | |
| Vertical flow direction | ISO294-4 | 0.70到1.1 | % | |
| Flow | ISO294-4 | 0.30到0.70 | % | |
| Melt Mass-Flow Rate | ASTMD1238 | 16 | g/10min | |
| Density / Specific Gravity | ASTMD792,ISO1183 | 1.53 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Break,23℃ | ASTMD638 | 2.0 | % | |
| ASTMD638 | 134 | Mpa | ||
| fracture | ISO527-2/1A/5 | 2.5 | % | |
| ISO527-2/1A/5 | 130 | Mpa | ||
| Flexural Modulus | 23°C | ISO178 | 9700 | Mpa |
| Flexural Stress | 23°C | ISO178 | 210 | Mpa |
| 23°C | ASTMD638 | 9650 | Mpa | |
| 断裂,-40°C | ASTMD638 | 190 | Mpa | |
| ASTMD638 | 1.9 | % | ||
| 断裂,0°C | ASTMD638 | 1.9 | % | |
| ASTMD638 | 159 | Mpa | ||
| 断裂,80°C | ASTMD638 | 77.2 | Mpa | |
| ASTMD638 | 3.9 | % | ||
| 断裂,121°C | ASTMD638 | 4.3 | % | |
| ASTMD638 | 61.4 | Mpa | ||
| -40°C | ASTMD638 | 11000 | Mpa | |
| 0°C | ASTMD638 | 10500 | Mpa | |
| 80°C | ASTMD638 | 4830 | Mpa | |
| 121°C | ASTMD638 | 3760 | Mpa | |
| -- | ISO527-2/1A/1 | 9200 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO306/B50 | 220 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1E-04 | cm/cm/°C | |
| 8.0Mpa, Unannealed | ISO75-2/C | 150 | °C | |
| Glass Transition Temperature | ISO11357-2 | 60.0 | °C | |
| 0.45MPa Annealed | ASTMD648 | 228 | °C | |
| Melting Temperature | ISO11357-3,ASTMD3418 | 225 | °C | |
| 0.45MPa, Unannealed | ISO75-2/B | 225 | °C | |
| 1.8MPa, Unannealed | ISO75-2/A | 205 | °C | |
| ASTMD648 | 206 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | IEC60112 | 425 | V | |
| Surface Resistivity | IEC60093 | >1.0E+15 | ohms | |
| 1MHz | ASTMD150 | 3.70 | ||
| IEC60250 | 4.10 | |||
| ASTMD150,IEC60250 | 0.016 | |||
| 100Hz | IEC60250 | 2.2E-03 | ||
| IEC60250 | 4.50 | |||
| -- | IEC60243-1 | 31 | KV/mm | |
| ASTMD257 | 1E+15 | ohms·cm | ||
| IEC60093 | >1.0E+15 | ohms·cm | ||
| --3 | ASTMD149 | 22 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 45 | kJ/m² |
| 23°C | ISO179/1eU | 46 | kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.5 | kJ/m² |
| -30°C | ISO179/1eA | 8.5 | kJ/m² | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 7.5 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Sale | ISO2039-2 | 90 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.710mm | UL94 | HB | |
| Oxygen Index | ISO4589-2 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.