PBT VALOX™ VIC4311 BK1066L SABIC INNOVATIVE US
75
- Unit Price:
- $3750 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Electrical field Electronic field Electronic display Engine hood parts Automotive External Parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.20to0.40 | % |
MD:6.40mm | 内部方法 | 0.60to0.80 | % | |
TD:3.20mm | 内部方法 | 0.60to0.80 | % | |
Moisture Absorption | Saturation,23°C | ISO62 | 0.090 | % |
Equilibrium,23°C,50%RH | ISO62 | 0.070 | % | |
Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 19 | g/10min |
Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 15.6 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Modulus | ISO527-2/1 | 7380 | Mpa | |
Tensile Stress | Yield | ISO527-2/5 | 86.5 | Mpa |
Break | ISO527-2/5 | 84.0 | Mpa | |
Tensile Strain | Yield | ISO527-2/5 | 3.0 | % |
Break | ISO527-2/5 | 4.0 | % | |
Tensile Elongation | Yield | ASTMD638 | 3.0 | % |
Tensile Modulus | ASTMD638 | 8370 | Mpa | |
Tensile Strength | Break | ASTMD638 | 84.0 | Mpa |
Yield | ASTMD638 | 83.0 | Mpa | |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 6080 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 129 | Mpa |
Flexural Strength | ISO178 | 139 | Mpa | |
Tensile Elongation | Break | ASTMD638 | 4.0 | % |
Flexural Modulus | ISO178 | 6190 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 175 | °C |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831 | 2.3E-05 | cm/cm/°C |
MD:-30to30°C | ASTME831 | 3E-05 | cm/cm/°C | |
MD:-40to40°C | ISO11359-2 | 2.3E-05 | cm/cm/°C | |
TD:-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
TD:-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 220 | °C |
1.8MPa,Unannealed,3.20mm | ASTMD648 | 205 | °C | |
Ball PressureTest | 75°C | IEC60695-10-2 | Pass | |
Vicat Softening Temperature | ASTMD152510 | 180 | °C | |
-- | ISO306/B50 | 175 | °C | |
-- | ISO306/B120 | 170 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Surface Resistivity | ASTMD257 | 1E+16 | ohms | |
Dielectric Constant | 50Hz | ASTMD150 | 3.00 | |
60Hz | ASTMD150 | 3.00 |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 16 | kJ/m² |
Notched Izod Impact Strength | -30°C | ISO180/1A | 9.9 | kJ/m² |
23°C | ISO180/1A | 13 | kJ/m² | |
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 13.9 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.