PBT Cristin® ST820 BK503 DUPONT USA
31
- Unit Price:
- $4095 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1220 | ||
| Modeling Shrinkage | ASTM D955 | 1.7 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | -，平行Flow | cm/cm | ASTM D955 | |
| -，垂直Flow | cm/cm | ASTM D955 | ||
| TD | ISO294-4 | 1.7 | % | |
| MD | ISO294-4 | 1.8 | % | |
| Ejection Temperature | 170 | °C |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal Tensile Strain at Break | ISO527-2 | >50 | % | |
| Unnotched Izod Impact Strength | -，-40 ℃, 0.00 mm | J/m | ASTM D256 | No Break |
| -，23 ℃, 0.00 mm | J/m | ASTM D256 | No Break | |
| Tensile Elongation?(Break) | 23℃, 0.00 mm, Compression Molded, Type I | % | ASTM D638 | 150 |
| Flexural Stress | ISO178 | 50.0 | Mpa | |
| Notched Impact Strength | 23℃, 0.00 mm, 0.0 mm, Injection Molded, Method A, Across Flow | J/m | ASTM D256 | No Break |
| Tensile Stress | Yield | ISO527-2 | 36.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 7.0 | % |
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 130 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 1600 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 1600 | Mpa | ||
| Flexural Modulus | 23 ℃, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant | MPa | ASTM D790 | 1680 |
| ISO178 | 1500 | Mpa | ||
| Flexural Strength | 23 ℃, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I | MPa | ASTM D790 | 53 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | ASTM D648/ISO 75 | 100 | ℃（℉） | |
| ASTM D648/ISO 75 | 145 | ℃（℉） | ||
| 0.45MPa,Unannealed | ISO75-2/B | 100 | °C | |
| 0.45MPa,Annealed | ISO75-2/B | 145 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 50.0 | °C | |
| Melting Temperature | 225 | ℃（℉） | ||
| ℃ | DSC | 225 | ||
| Melting Temperature | ISO11357-3 | 225 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod impact strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FMVSS Flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Burning Rate | 1.00mm | ISO3795 | 38 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.