- Unit Price:
- $2869 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 42MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Fast forming cycle
- Application Areas:Automotive sector
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.0 | % |
| MD:3.00mm4 | 内部方法 | 0.40 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.080 | % |
| 23℃, 24 hr | ISO 62 | 0.080 | % | |
| Shrinkage rate 2 | TD: 3.00 mm | Internal Method | 1.0 | % |
| MD: 3.00 mm | Internal Method | 0.40 | % | |
| Flow Length 3 | 250℃, 1.00 mm | Internal Method | 7.00 | CM |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23℃ | ISO 527-2 | 8400 | Mpa |
| 23°C | ISO527-2 | 8400 | Mpa | |
| Bending modulus | 23℃ | ISO 178 | 7900 | Mpa |
| 23°C | ISO178 | 7900 | Mpa | |
| bending strength | 23℃ | ISO 178 | 195 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2 | 125 | Mpa |
| Yield, 23℃ | ISO 527-2 | 125 | Mpa | |
| Tensile strain | Break, 23℃ | ISO 527-2 | 3.0 | % |
| Break,23°C | ISO527-2 | 3.0 | % | |
| Bending stress | 23°C | ISO178 | 195 | Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 12 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | ||
| Linear expansion coefficient - flow | -30 to 100℃ | ISO 11359-2 | 0.000042 | cm/cm/℃ |
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 4.2E-05 | cm/cm/°C |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 208 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 208 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength4 | 250°C,1.00mm | 内部方法 | 7.00 | CM |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.