Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:2.00mm | | 0.40 | % |
Modeling Shrinkage | 吸水率(Saturation,23°C) | | 0.070 | % |
Modeling Shrinkage | TD:2.00mm | | 1.1 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strain | Break | ISO527-2 | 2.0 | % |
Flexural Modulus | | ISO178 | 10500 | Mpa |
Flexural Stress | | ISO178 | 210 | Mpa |
Tensile Stress | Break | ISO527-2 | 135 | Mpa |
Tensile Modulus | | ISO527-2 | 11000 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:-30to50°C | ISO11359-2 | 2E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 208 | °C |
Linear thermal expansion coefficient | TD:50to120°C | ISO11359-2 | 1.4E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 224 | °C |
Linear thermal expansion coefficient | TD:-30to50°C | ISO11359-2 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:-30to120°C | ISO11359-2 | 2E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-30to120°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | >220 | °C |
Linear thermal expansion coefficient | MD:50to120°C | ISO11359-2 | 2E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 6E+15 | ohms |
Dissipation Factor? | 1MHz | IEC60250 | 0.014 | |
Comparative Tracking Index | CTI | UL746 | PLC3 | |
Relative Permittivity | 1MHz | IEC60250 | 3.90 | |
Volume Resistivity | | IEC60093 | 5E+16 | ohms·cm |
Dielectric Strength | 1.00mm | IEC60243-1 | 24 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 45 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.