Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:2.00mm | | 0.80 | % |
Modeling Shrinkage | MD:2.00mm | | 0.40 | % |
Modeling Shrinkage | 吸水率(Saturation,23°C) | | 0.070 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2 | 130 | Mpa |
Tensile Strain | Break | ISO527-2 | 2.0 | % |
Tensile Modulus | | ISO527-2 | 10500 | Mpa |
Flexural Modulus | | ISO178 | 9000 | Mpa |
Flexural Stress | | ISO178 | 190 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:-30to50°C | ISO11359-2 | 1E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:-30to120°C | ISO11359-2 | 1E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:50to120°C | ISO11359-2 | 1E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-30to50°C | ISO11359-2 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-30to120°C | ISO11359-2 | 1E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD:50to120°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 224 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 194 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 5E+15 | ohms |
Volume Resistivity | | IEC60093 | 9E+16 | ohms·cm |
Dielectric Strength | 1.00mm | IEC60243-1 | 28 | KV/mm |
Dielectric Strength | 2.00mm | IEC60243-1 | 24 | KV/mm |
Relative Permittivity | 1MHz | IEC60250 | 3.40 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.020 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 52 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.