Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
Modeling Shrinkage | TD | ISO294-4 | 1.0to1.2 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.30to0.40 | % |
SpecificHeatCapacityofMelt | | 内部方法 | 1720 | J/kg/°C |
ThermalConductivityofMelt | | 内部方法 | 0.17 | W/m/K |
Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 9.00 | cm3/10min |
DensityofMelt | | 内部方法 | 1.320 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Creep Modulus | 1hr | ISO899-1 | 9200 | Mpa |
Tensile Creep Modulus | 1000hr | ISO899-1 | 6500 | Mpa |
Flexural Stress | 23°C | ISO178 | 210 | Mpa |
Tensile Stress | Break | ISO527-2/1A/5 | 150 | Mpa |
Tensile Strain | Break | ISO527-2/1A/5 | 2.5 | % |
Tensile Modulus | | ISO527-2/1A/1 | 10300 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 225 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 210 | °C |
Deflection Temperature Under Load? | 8.0MPa,Unannealed | ISO75-2/C | 150 | °C |
Vicat Softening Temperature | | ISO306/B50 | 220 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 2.5E-05 | cm/cm/°C |
Melting Temperature | | ISO11357-3 | 225 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Relative Permittivity | 100Hz | IEC60250 | 4.40 | |
Relative Permittivity | 1MHz | IEC60250 | 4.30 | |
Comparative Tracking Index | | IEC60112 | 425 | V |
Dielectric Strength | | IEC60243-1 | 33 | KV/mm |
Dissipation Factor? | 100Hz | IEC60250 | 2E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.019 | |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 60 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 60 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.2mm | UL94 | HB | |
UL flame retardant rating | 1.5mm | UL94 | HB | |
Oxygen Index | | ISO4589-2 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.