PBT VALOX™ V4860HR SABIC INNOVATIVE US

Unit Price:
$9415 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD：3.20mm	内部方法	0.50to1.0	%
Modeling Shrinkage	Modeling Shrinkage	MD：3.20mm	内部方法	0.50to0.70	%
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.060	%
Moisture Absorption	Moisture Absorption	Saturation,23°C	ISO62	0.19	%
Melt Mass-Flow Rate	250°C/5.0kg	ASTMD1238	18	g/10min
Melt Volume flow Rate	250°C/5.0kg	ISO1133	12.4	cm3/10min
Density / Specific Gravity		ASTMD792	1.64	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.64	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Strain (Break)		ISO178	2.9	%
Flexural Stress	--6	ISO178	182	Mpa
Flexural Stress	Flexural Stress	--7	ISO178	183	Mpa
Tensile Modulus		ISO527-2/1	9450	Mpa
Tensile Elongation	Break	ASTMD638	2.3	%
Flexural Modulus		ISO178	7880	Mpa
Flexural Strength	Break,50.0mmSpan	ASTMD790	2.96	Mpa
Tensile Elongation	Yield	ASTMD638	2.3	%
Tensile Modulus		ASTMD638	9750	Mpa
Tensile Strength	Yield	ASTMD638	116	Mpa
Tensile Strength	Tensile Strength	Break	ASTMD638	115	Mpa
Flexural Modulus	50.0mmSpan	ASTMD790	6740	Mpa
Flexural Strength	Yield,50.0mmSpan	ASTMD790	174	Mpa
Tensile Stress	Break	ISO527-2/5	111	Mpa
Tensile Stress	Tensile Stress	Yield	ISO527-2/5	112	Mpa
Tensile Strain	Yield	ISO527-2/5	2.1	%
Tensile Strain	Tensile Strain	Break	ISO527-2/5	2.2	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	MD：-40to95°C	ASTME831	2.4E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD：23to80°C	ISO11359-2	2.3E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40to95°C	ASTME831	1.1E-04	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to80°C	ISO11359-2	1.2E-04	cm/cm/°C
Deflection Temperature Under Load?	0.45MPa,Unannealed,6.40mm	ASTMD648	221	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	197	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,6.40mm	ASTMD648	205	°C
Vicat Softening Temperature		ASTMD152512	176	°C
	Vicat Softening Temperature	--	ISO306/B50	176	°C
	Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	175	°C
Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	188	°C
Ball PressureTest	75°C	IEC60695-10-2	Pass

Impact Properties	Test Condition	Test Method	Test Result	Unit
Notched Izod Impact Strength	-30°C	ASTMD256	74	J/m
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ASTMD256	90	J/m
CharpyNotchedImpactStrength9	23°C	ISO179/1eA	11	kJ/m²
Notched Izod Impact Strength	-30°C	ISO180/1A	8.5	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	10	kJ/m²
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	13.4	J

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.8mm,TestingbySABIC	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.