PBT Cristin® SK603 BK851 DUPONT USA
110
- Unit Price:
- $3140 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 34.9MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf Good strength (glass fibe 20% by weight ratio) 20% filler by weight
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| -，Across Flow | % | ISO 294-4 | 1.0 | |
| -，Flow | % | ISO 294-4 | ||
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 0.40 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.15 | % | |
| -，23C/59RH | % | ISO 62 | 0.15 | |
| -，Sat/23C | % | ISO 62 | ||
| MediumDensity | 1.26 | g/cm³ | ||
| Top out temperature | 170 | °C | ||
| SpecificHeatCapacity of Melt | 1860 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.25 | W/m/K | ||
| Density/specific gravity | g/cm | ISO 1183 | 1.45 | |
| ISO1183 | 1.45 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy non notched impact strength | -，-30℃, Type 1, Edgewise | KJ/m | ISO 179 | 54 |
| -，23 ℃, Type 1, Edgewise | KJ/m | ISO 179 | 56 | |
| Charpy notch impact strength | -，-30 ℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 9.8 |
| -，23℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | 7.5 | |
| Non notched impact strength | 23 ℃, Type 1 | KJ/m | ISO 180 | 44 |
| TensileCreepModule | 1hr | ISO899-1 | 7200 | Mpa |
| Fracture point tensile strain | 23℃ | % | ISO 527-1, -2 | 3.2 |
| Fracture point tensile stress | 23℃ | MPa | ISO 527-1, -2 | |
| Tensile stress | Break | ISO527-2 | 120 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.2 | % |
| Bending stress | ISO178 | 180 | Mpa | |
| Gap impact strength | 23 ℃, Type 1, Notch A | KJ/m | ISO 180 | |
| Tensile creep modulus | -，1h | MPa | ISO 899-1 | 7200 |
| -，1000h | MPa | ISO 899-1 | ||
| 1000hr | ISO899-1 | 5600 | Mpa | |
| Tensile modulus | 23℃ | MPa | ISO 527-1, -2 | 7400 |
| ISO527-2 | 7000 | Mpa | ||
| Bending modulus | 23℃ | MPa | ISO 178 | 6200 |
| ISO178 | 6500 | Mpa | ||
| bending strength | 23℃ | MPa | ISO 178 | 180 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | -，0.45 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | |
| -，1.80 Mpa，Unannealed | ℃ | ISO 75B-1, -2 | 204 | |
| 0.45MPa,Unannealed | ISO75-2/B | 220 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 204 | °C | |
| Flame retardant grade | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD | ISO11359-2 | 1E-04 | cm/cm/°C | |
| Melting temperature | ℃ | ISO 3146 | 225 | |
| Vicat softening temperature | ISO306/B50 | 210 | °C | |
| Melting temperature 2 | ISO11357-3 | 224 | °C | |
| Linear coefficient of thermal expansion | 平行Flow ，23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | |
| 垂直Flow ，23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | 0.000040 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.60 | ||
| Leakage Trace Index | IEC60112 | 350 | V | |
| Dissipation factor | 100Hz | IEC60250 | 1.2E-03 | |
| 1MHz | IEC60250 | 0.019 | ||
| Dielectric strength | IEC60243-1 | 29 | KV/mm | |
| Surface resistivity | IEC60093 | 1E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | -30°C | ISO180/1U | 60 | kJ/m² |
| 23°C | ISO180/1U | 60 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 55 | kJ/m² |
| 23°C | ISO179/1eU | 60 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 8.0 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 8.0 | kJ/m² |
| 23°C | ISO180/1A | 9.0 | kJ/m² |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | % | ISO 4589-1, -2 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 19 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate)4 | ISO6452 | 1E-04 | g |
| Burning rate 3 | 1.00mm | ISO3795 | 28 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 140 | µgC/g | |
| Odor | VDA270 | 3.00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.