Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 19.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2/1A/5 | 135 | Mpa |
Tensile Strain | Break | ISO527-2/1A/5 | 3.0 | % |
Tensile Modulus | | ISO527-2/1A/1 | 7800 | Mpa |
Flexural Stress | 23°C | ISO178 | 175 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO306/B50 | 220 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 3.5E-05 | cm/cm/°C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 195 | °C |
Deflection Temperature Under Load? | 8.0MPa,Unannealed | ISO75-2/C | 95.0 | °C |
Melting Temperature | | ISO11357-3 | 255 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Dissipation Factor? | 1MHz | IEC60250 | 0.018 | |
Dissipation Factor? | 100Hz | IEC60250 | 1.3E-03 | |
Dielectric Strength | | IEC60243-1 | 29 | KV/mm |
Relative Permittivity | 100Hz | IEC60250 | 4.40 | |
Relative Permittivity | 1MHz | IEC60250 | 4.10 | |
Comparative Tracking Index | | IEC60112 | 250 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 43 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 43 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.6mm | UL94 | HB | |
UL flame retardant rating | 0.8mm | UL94 | HB | |
Oxygen Index | | ISO4589-2 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.